Magnetron sıçratma ile Tantal-Oksit kaplama öncesi uygulanan alkali, alkali-asit ve kumlama yüzey işlemlerinin 7075 Alüminyum alaşımlarının aşınma davranışlarına etkileri

Canser GÜL, (Department of Metallurgy and Materials Engineering, Manisa Celal Bayar University, Engineering Faculty, Manisa, Türkiye)
Sevda ALBAYRAK, (Department of Metallurgy and Materials Engineering, Gazi University, Technology Faculty, Ankara, Türkiye)
Hanifi ÇİNİCİ, (Department of Metallurgy and Materials Engineering, Gazi University, Technology Faculty, Ankara, Türkiye)
İrem Burcu Algan Şimşek (Department of Metallurgy and Materials Engineering, Gazi University, Technology Faculty, Ankara, Türkiye)
Gazi Üniversitesi Mühendislik Mimarlık Fakültesi Dergisi
1 0
Yıl: 2023 Cilt: 38 Sayı: 2 Sayfa Aralığı: 795 - 806 Metin Dili: Türkçe DOI: 10.17341/gazimmfd.1024352 İndeks Tarihi: 13-03-2023

Magnetron sıçratma ile Tantal-Oksit kaplama öncesi uygulanan alkali, alkali-asit ve kumlama yüzey işlemlerinin 7075 Alüminyum alaşımlarının aşınma davranışlarına etkileri

Öz:
Alüminyum alaşımları yüksek özgül dayanımları nedeni ile birçok sektörde yaygın kullanım alanı olan ve günümüzün gelişen teknolojisine uyum sağlayabilmek için sürekli geliştirilmeye devam eden alaşımlardır. Bu alaşım grupları içinde çökelme sertleşmesi ile sertleştirilebilen alaşım gruplarından olan 2XXX ve 7XXX serisi alaşımlarının kullanımı daha da yaygındır. Bu çalışma kapsamında 7075 alüminyum alaşımlarının aşınma dayanımlarının geliştirilmesi amacı ile RF sıçratma yöntemi ile amorf tantal-oksit tabakası kaplanmıştır. Kaplama tabakası; parlak, kumlanmış, alkali ve alkali asit işlemleri sonrasında numune gruplarına uygulanmış olup, kaplama öncesi uygulanan yüzey işlemlerinin kaplama sonrası aşınma performanslarına etkisi incelenmiştir. Kaplama sonrası yüzey morfolojilerine olan etki taramalı elektron mikroskobu (SEM) ve enerji dağılım spektroskopisi (EDS) kullanılarak, yapısal analizleri X-ışını difraksiyonu (XRD) yöntemi ile incelenmiştir. Numunelerin aşınma davranışı oda sıcaklığında kuru kayma koşullarında gerçekleştirilen ball-on disk aşınma testi ile ve aşınma sonrasında gerçekleştirilen SEM incelemeleri, aşınma izi profil ölçümleri, ortalama hacim kaybı hesapları ve sürtünme katsayısı değerlendirmeleri ile gerçekleştirilmiştir. Kaplama işlemi sonrasında, çatlak, boşluk ve heterojenlik içermeyen amorf yapıda Ta2O5 eldesi sağlanmıştır. Kaplama kalınlıkları ≅2,5-5µm olarak ölçülmüştür. Tüm numuneler arasında en yüksek aşınma dayanımı alkali ve alkali asit işlemleri sonrasında kaplanmış olan numunelerde gözlemlenmiş olup, parlatılmış ve işlem görmemiş numune ile kıyaslandığında aşınma sonrası hacim kayıplarının %69-77 oranında azaldığı gözlemlenmiştir.
Anahtar Kelime: Alüminyum alaşımı AA7075 Tantal-oksit RF sıçratma yöntemi Yüzey işlemi Aşınma

The effects of alkali, alkali-acid and sandblasting surface treatments applied before Tantalum-Oxide coating with magnetron sputtering on the wear behavior of 7075 Aluminum alloys

Öz:
Aluminum alloys are alloys that are widely used in many sectors due to their high specific strength and are constantly being developed to adapt to today's developing technology. Among these alloy groups, the use of 2XXX and 7XXX series alloys, which are alloy groups that can be hardened by precipitation hardening, is even more common. In this study, an amorphous tantalum-oxide layer was coated by magnetron sputtering method in order to improve the wear resistance of 7075 aluminum alloys. It was applied to the sample groups after polished, sandblasted, alkali, and alkali acid treatments, and the effect of the surface treatments applied before coating on the wear performances after coating was investigated. The effect on the surface morphologies after coating was investigated using scanning electron microscopy (SEM) and energy dispersion spectroscopy (EDS), and their structural analysis was investigated by the X-ray diffraction (XRD) method. The wear behavior of the samples was determined by the ball-on disc wear test performed at room temperature under dry sliding conditions and by SEM examinations, wear track profile measurements, average volume loss calculations and friction coefficient evaluations performed after wear. After the coating process, Ta2O5 coating was obtained in an amorphous structure without cracks, voids, and heterogeneity. Coating thicknesses were measured as ≅2.5-5μm. The highest wear resistance among all samples was observed in the samples coated after alkali and alkali acid treatments, and it was observed that the volume losses after wear decreased by 69-77% compared to the polished and untreated sample.
Anahtar Kelime: Aluminum alloys AA7075 tantalum-oxide magnetron sputtering method surface treatment wear

Belge Türü: Makale Makale Türü: Araştırma Makalesi Erişim Türü: Erişime Açık
  • Yağcı T., Cöcen Ü., Çulha O., Korkmaz A., Alüminyum Döküm Alaşımlarına Dair Son Yıllardaki Akademik Ve Endüstriyel Gelişmelere Genel Bakış Ve Değerlendirme, Uludağ Üniversitesi Mühendislik Fakültesi Dergisi, 26 (3), 1191-1210, 2021.
  • Pul M., Özerkan H.B., The effect of cutting depth and cutting tool geometry on surface roughness and tool wear behavior in the machining of Al 6061 alloy, Journal of the Faculty of Engineering and Architecture of Gazi University, 37 (4), 2013-2024, 2022.
  • Nguyen C.L., Preston A., Tran A.T.T., Dickinson M., Metson J.B., Adhesion enhancement of titanium nitride coating on aluminum casting alloy by intrinsic microstructures, Applied Surface Science, 377, 174- 179, 2016.
  • Durmuş H., Gül C., Çömez N., Uzun R.O., From Metal Chips to Composite: Effect of age-hardening on mechanical and wear properties of Al2O3 reinforced AA7075 composites, Science of Sintering, 52, 177-186, 2020.
  • Dwivedi P., Siddiquee A.N., Maheshwari S., Issues and Requirements for Aluminum Alloys Used in Aircraft Components: State of the Art, Russian Journal of Non-Ferrous Metals, 62, 212–225, 2021.
  • Chandradass J., Thirugnanasambandham T., Jawahar P., Kannan T.T.M., Effect of silicon carbide and silicon carbide/alumina reinforced aluminum alloy (AA6061) metal matrix composite, Materials Today: Proceedings, 45 (7), 7147-7150, 2021.
  • Abolhasani A., Zarei-Hanzaki A., Abedi H.R., Rokni M.R., The room temperature mechanical properties of hot rolled 7075 aluminum alloy, Materials and Design, 34, 631-636, 2012.
  • Kılıç S., Kacar İ., Öztürk F., New trend in aerospace industry: Al-Li based alloys, Journal of the Faculty of Engineering and Architecture of Gazi University, 34 (1), 275-296, 2019.
  • Hekimoğlu A.P., Turan Y.E., İsmailoğlu İ.İ., Akyol M.E., Şen E., Effect of grain refinement with boron on the microstructure and mechanical properties of Al-30Zn alloy, Journal of the Faculty of Engineering and Architecture of Gazi University, 34 (1), 523-534, 2019.
  • Demirel M.Y., Karaağaç İ., 7075-T6 Alaşımının Mikroyapı ve Mekanik Özelliklerine Tavlama İşleminin Etkisinin Deneysel Olarak Araştırılması, Politeknik Dergisi, 2 3(2), 283-289, 2020.
  • Dobrzański L.A., Włodarczyk A., Adamiak M., Structure, properties and corrosion resistance of PM composite materials based on EN AW- 2124 aluminum alloy reinforced with the Al2O3 ceramic particles, Journal of Materials Processing Technology, 162–163, 27-32, 2005.
  • Karacif K., Hardness and corrosion properties of functionally graded AA5083/Al2O3 composites produced by powder metallurgy method, International Journal of Materials Research, 111 (9), 719-725, 2020.
  • Uzun A., Asikuzun E., Gokmen U., Cinici H., Vickers Microhardness Studies on B4C Reinforced/Unreinforced Foamable Aluminium Composites, Transactions of the Indian Institute of Metals, 71, 327-337, 2018.
  • Shanbhag V.V., Yalamoori N.N., Karthikeyan S., Ramanujam R., Venkatesan K., Fabrication, surface morphology and corrosion investigation of Al 7075-Al2O3 matrix composite in sea water and industrial environment, Procedia Engineering, 97, 607-613, 2014.
  • Devaneyan S.P., Pushpanathan D.P., Senthilvelan T., Ganesh R., Enhanced corrosion and wear behavior of nano titanium carbide reinforced polyurethane PMC coating on aluminium 7075, Materials Today: Proceedings, 5 (5), Part 2, 11491-11497, 2018.
  • Zhang Z.H., Liu S.F., Sun Z.M., Yan X.D., Evaluation on Microstructure of Aluminum Alloys Dedicated to Plasma Etcher, Materials Science Forum, 689, 343–349, 2011.
  • Kehal A., Saoula N., Abaidia S.-E.-H., Nouveau C., Effect of Ar/N2 flow ratio on the microstructure and mechanical properties of Ti-Cr-N coatings deposited by DC magnetron sputtering on AISI D2 tool steels, Surface and Coatings Technology, 421, 127444, 2021.
  • Poolcharuansin P., Chingsungnoen A., Passaja N., Horprathum M., Bradley J.W., Measurement of negative ion fluxes during DC reactive magnetron sputtering of Ti in Ar/O2 atmosphere using a magnetic- filtering probe, Vacuum, 194, 110549, 2021.
  • Al-Kuhaili M.F., Co-sputtered tantalum-doped tin oxide thin films for transparent conducting applications, Materials Chemistry and Physics, 257, 123749, 2021.
  • Zhou D., Huang L., Yuan J., Li C., Influences of different sputtering current on the microstructure and electrical properties of silicon nitride thin films deposited on cemented carbide tools, Ceramics International, 47(22), 32160-32167, 2021.
  • Mu J., Wang H., Qin B., Zhang Y., Chen L., Zeng C., Improved wear and corrosion resistance of biological compatible TiZrNb films on biomedical Ti6Al4V substrates by optimizing sputtering power, Surface and Coatings Technology, 428, 127866, 2021.
  • Wei B.-J., Cheng Y.-L., Liu Y.-Y., Zhu Z.-D., Cheng Y.-L., Corrosion and wear resistance of AZ31 Mg alloy treated by duplex process of magnetron sputtering and plasma electrolytic oxidation, Transactions of Nonferrous Metals Society of China, 31 (8), 2287-2306, 2021.
  • Sheng L., Xiao Y., Jiao C., Du B., Li Y., Wu Z., Shao L., Influence of layer number on microstructure, mechanical properties and wear behavior of the TiN/Ti multilayer coatings fabricated by high-power magnetron sputtering deposition, Journal of Manufacturing Processes, 70, 529-542, 2021.
  • Ma Y., Li L., Qian J., Qu W., Luo R., Wu F., Chen R., Materials and structure engineering by magnetron sputtering for advanced lithium batteries, Energy Storage Materials, 39, 203-224, 2021.
  • Zlamal T., Mrkvica I., Szotkowski T., Malotova S., The Influence of Surface Treatment of PVD Coating on Its Quality and Wear Resistant, Coatings, 9 (7), 439., 2019.
  • Fernández-Abia A.I., Barreiro J., López de Lacalle L.N., González- Madruga D., Effect of mechanical pre-treatments in the behaviour of nanostructured PVD-coated tools in turning, The International Journal of Advanced Manufacturing Technology, 73 (5-8), 1119-1132, 2014.
  • Gül C., Albayrak S., Çinici H., Characterization of Tantalum Oxide Sol–Gel-coated AZ91 Mg Alloys, Transactions of the Indian Institute of Metals, 73, 1249–1256, 2020.
  • Wang X., Zeng X., Wu G., Yao S., Lai Y., Effects of tantalum ion implantation on the corrosion behavior of AZ31 magnesium alloys, Journal of Alloys and Compounds, 437 (1-2), 87-92, 2007.
  • Bansal N. P., Low-temperature synthesis, pyrolysis and crystallization of tantalum oxide gels, Journal of Material Science, 29, 5065–5070, 1994.
  • Ye D., Xu Z., Pan J., Yin C., Hu D., Wu Y., Li R., Li Z., Prediction and Analysis of the Grit Blasting Process on the Corrosion Resistance of Thermal Spray Coatings Using a Hybrid Artificial Neural Network, Coatings, 11, 1274, 2021.
  • Sen D., Chavan N.M., Rao D.S., Sundararajan G., Influence of grit blasting on the roughness and the bond strength of detonation sprayed coating, Journal of Thermal Sprey Technology, 19, 805–815, 2010.
  • Multigner M., Ferreira-Barragans S., Frutos E., Jaafar M., Ibanez J., Marin P., Perez-Prado M.T., Gonzalez-Doncel G., Asenjo A., Gonzalez-Carrasco J.L., Superficial severe plastic deformation of 316 LVM stainless steel through grit blasting: Effects on its microstructure and subsurface mechanical properties, Surface and Coatings Technology, 205, 1830–1837, 2010.
  • Yurddaşkal M., Durmuş H., The Effects of Acid Concentration, Etching Temperature and Time on The Surface Morphologies of Ti6Al4V, European Journal of Technique, 10 (2), 388-394, 2020.
  • Liu W., Sun L., Luo Y., Wu R., Jiang H., Chen Y., Zeng G., Liu Y., Facile transition from hydrophilicity to superhydrophilicity and superhydrophobicity on aluminum alloy surface by simple acid etching and polymer coating, Applied Surface Science, 280, 193-200, 2013.
  • Di C., Yan X., Yang Y., Ye W., Zhao M., Li D., Wear behaviors and high-temperature oxidation resistance properties of tantalum carbide layer, Ceramics International, 47 (23), 32766-32774, 2021.
  • Durmuş H., Türkmen M., Çalıgülü U., Wear Resistances of X6Cr17 Ferritic Stainless-Steel Surfaces Coated with Al2O3 Powders Using Thermal Spray Method, Dicle Üniversitesi Mühendislik Fakültesi Mühendislik Dergisi, 11 (3), 1167-1173, 2020.
  • Huang H.L, Chang Y.Y., Chen H.J., Chou Y. K., Lai C.H., Chen M.Y.C., Antibacterial properties and cytocompatibility of tantalum oxide coatings with different silver content, Journal of Vacuum Science & Technology, A32, 02B117, 2014.
  • Yang Y.H., Chen D.J., Wu F.B., Microstructure, hardness, and wear resistance of sputtering TaN coating by controlling RF input power, Surface and Coatings Technology, 303, 32-40, 2016.
  • Ding Z., Tang Y., Liu L., Ding Z., Tan Y., He Q., Improving the adhesive, mechanical, tribological properties and corrosion resistance of reactive sputtered tantalum oxide coating on Ti6Al4V alloy via introducing multiple interlayers, Ceramics International, 48 (5), 5983- 5994, 2022.
  • Krainer S., Hirn U., Contact angle measurement on porous substrates: Effect of liquid absorption and drop size, Colloids and Surfaces A: Physicochemical and Engineering Aspects, 619, 126503, 2021.
  • Abouarkoub A., Thompson G., Zhou X., Scamans G., The influence of heat treatment on the caustic etching behaviour of the automotive AA6111 alloy, Journal of Minerals and Materials Characterization and Engineering, 4, 64, 2016.
  • Koroleva E., Thompson G., Hollrigl G., Bloeck M., Surface Morphological Changes of Aluminium Alloys in Alkaline Solution: Effect of Second Phase Material, Corrosion Science, 41, 1475-1495, 1999.
  • Guminsky R., Sheasby P., Lamb H., Reaction Rates of Second Phase Constituents in Aluminium during Etching, Brightening and Oxalic Acid Anodizing. Transaction of the Institute of Metal Finishing, 46, 44- 48, 1968.
  • Short E., Sheasby P., Reaction of Second Phase Constituents in Aluminium during Etching in Sodium Hydroxide Based Solutions. Transactions of the Institute of Metal Finishing, 47, 27-30, 1969.
  • Hu Y., Yuan B., Cheng F., Hu X., NaOH etching and resin pre-coating treatments for stronger adhesive bonding between CFRP and aluminium alloy, Composites Part B: Engineering, 178, 107478, 2019.
  • Soares E., Bouchonneau N., Alves A., Alves K., Filho O.A., Mesguich D., Chevallier G., Laurent C., Estournes C., Microstructure and mechanical properties of AA7075 aluminum alloy fabricated by spark plasma sintering (SPS), Materials, 14 (2), 488-493, 2021.
  • Bayazid S.M., Farhangi H., Asgharzadeh H., Radan L., Ghahramani A., Mirhaji A., Effect of cyclic solution treatment on microstructure and mechanical properties of friction stir welded 7075 Al alloy, Materials Science & Engineering A, 649, 293-300, 2016.
  • Wang Z., Georgarakis K., Nakayama K.S., Li Y., Tsarkov A.A., Xie G., Dudina D., Louzguine-Luzgin D.V., Yavari A.R., Microstructure and mechanical behavior of metallic glass fiber reinforced Al alloy matrix composites, Scientific Reports, 6, 24384, 2016.
  • Chen X, Bai R, Huang M., Optical properties of amorphous Ta2O5 thin films deposited by RF magnetron sputtering, Optical Materials, 97, 109404, 2019.
  • Grilli M.L., Yilmaz M., Aydogan S., Çırak B. B., Room temperature deposition of XRD-amorphous TiO2 thin films: investigation of device performance as a function of temperature, Ceramic International, 44, 11582–11590, 2018.
  • Bright T.J., Watjen J.I., Zhang Z.M., Muratore, C., Voevodin, A.A., Koukis, D.I., Tanner, D.B., Arenas, D.J., Infrared optical properties of amorphous and nanocrystalline Ta2O5 thin films, Journal of Applied Physics, 114, 083515, 2013.
  • Jimmy Wu S.-J., Houng B., Huang B.-S., Effect of growth and annealing temperatures on crystallization of tantalum pentoxide thin film prepared by RF magnetron sputtering method, Journal of Alloys and Compounds, 475, 488–493, 2009.
  • Kern M., Thompson V.P., Effects of sandblasting and silica-coating procedures on pure titanium, Journal of Dentistry, 22 (5), 300-306, 1994.
  • Schwankl M., Kellner R., Singer R.F., Körner C., The influence of sandblasting on the morphology of electroless deposited zinclayers on aluminum sheets, Applied Surface Science, 283, 202-208, 2013.
  • Wang H.-Y., Zhu R.-F., Lu Y.-P., Xiao G.-Y., Zhao X.-C., He K., Yuan Y.F., Li Y., Ma X.-N., Preparation and properties of plasma electrolytic oxidation coating on sandblasted pure titanium by a combination treatment, Materials Science and Engineering: C, 42, 657-664, 2014.
  • Hutchings I.M., Tribology: Friction and Wear of Engineering Materials Edward Arnold, London (1992).
  • Zhao Y., Zhang Z., Dai Q., Lin D., Li S., Microstructure and bond strength of HA (+ ZrO2+ Y2O3)/Ti6Al4V composite coatings fabricated by RF magnetron sputtering, Surface and Coatings Technology, 200, 5354-5363, 2006.
  • Ding S.J., Ju C.P., Lin J.H.C., Characterization of hydroxyapatite and titanium coatings sputtered on Ti-6Al-4V substrate, Journal of Materials Research, 44, 266-279, 1999.
  • Kelemen M., Schwarz-Selinger T., Mutzke A., Balden M., Vassallo E., Pedroni M., Dellasega D., Passoni M., Romeo F., Hakola A., Pelicon P., Zaplotnik R., Markelj S., Influence of surface roughness on the sputter yield of Mo under keV D ion irradiation, Journal of Nuclear Materials, 555, 153135, 2021.
  • Li C.P., Yang B.H., Wang X.C., Wang F., Li M.J., Su L., Li X.M., Influence of sputter-etching of substrate on the microstructural and optical properties of ZnO films deposited by RF magnetron sputtering, Applied Surface Science, 257 (14), 5998-6003, 2011.
APA Gül C, Albayrak S, ÇİNİCİ H, algan şimşek i (2023). Magnetron sıçratma ile Tantal-Oksit kaplama öncesi uygulanan alkali, alkali-asit ve kumlama yüzey işlemlerinin 7075 Alüminyum alaşımlarının aşınma davranışlarına etkileri. , 795 - 806. 10.17341/gazimmfd.1024352
Chicago Gül Canser,Albayrak Sevda,ÇİNİCİ Hanifi,algan şimşek irem burcu Magnetron sıçratma ile Tantal-Oksit kaplama öncesi uygulanan alkali, alkali-asit ve kumlama yüzey işlemlerinin 7075 Alüminyum alaşımlarının aşınma davranışlarına etkileri. (2023): 795 - 806. 10.17341/gazimmfd.1024352
MLA Gül Canser,Albayrak Sevda,ÇİNİCİ Hanifi,algan şimşek irem burcu Magnetron sıçratma ile Tantal-Oksit kaplama öncesi uygulanan alkali, alkali-asit ve kumlama yüzey işlemlerinin 7075 Alüminyum alaşımlarının aşınma davranışlarına etkileri. , 2023, ss.795 - 806. 10.17341/gazimmfd.1024352
AMA Gül C,Albayrak S,ÇİNİCİ H,algan şimşek i Magnetron sıçratma ile Tantal-Oksit kaplama öncesi uygulanan alkali, alkali-asit ve kumlama yüzey işlemlerinin 7075 Alüminyum alaşımlarının aşınma davranışlarına etkileri. . 2023; 795 - 806. 10.17341/gazimmfd.1024352
Vancouver Gül C,Albayrak S,ÇİNİCİ H,algan şimşek i Magnetron sıçratma ile Tantal-Oksit kaplama öncesi uygulanan alkali, alkali-asit ve kumlama yüzey işlemlerinin 7075 Alüminyum alaşımlarının aşınma davranışlarına etkileri. . 2023; 795 - 806. 10.17341/gazimmfd.1024352
IEEE Gül C,Albayrak S,ÇİNİCİ H,algan şimşek i "Magnetron sıçratma ile Tantal-Oksit kaplama öncesi uygulanan alkali, alkali-asit ve kumlama yüzey işlemlerinin 7075 Alüminyum alaşımlarının aşınma davranışlarına etkileri." , ss.795 - 806, 2023. 10.17341/gazimmfd.1024352
ISNAD Gül, Canser vd. "Magnetron sıçratma ile Tantal-Oksit kaplama öncesi uygulanan alkali, alkali-asit ve kumlama yüzey işlemlerinin 7075 Alüminyum alaşımlarının aşınma davranışlarına etkileri". (2023), 795-806. https://doi.org/10.17341/gazimmfd.1024352
APA Gül C, Albayrak S, ÇİNİCİ H, algan şimşek i (2023). Magnetron sıçratma ile Tantal-Oksit kaplama öncesi uygulanan alkali, alkali-asit ve kumlama yüzey işlemlerinin 7075 Alüminyum alaşımlarının aşınma davranışlarına etkileri. Gazi Üniversitesi Mühendislik Mimarlık Fakültesi Dergisi, 38(2), 795 - 806. 10.17341/gazimmfd.1024352
Chicago Gül Canser,Albayrak Sevda,ÇİNİCİ Hanifi,algan şimşek irem burcu Magnetron sıçratma ile Tantal-Oksit kaplama öncesi uygulanan alkali, alkali-asit ve kumlama yüzey işlemlerinin 7075 Alüminyum alaşımlarının aşınma davranışlarına etkileri. Gazi Üniversitesi Mühendislik Mimarlık Fakültesi Dergisi 38, no.2 (2023): 795 - 806. 10.17341/gazimmfd.1024352
MLA Gül Canser,Albayrak Sevda,ÇİNİCİ Hanifi,algan şimşek irem burcu Magnetron sıçratma ile Tantal-Oksit kaplama öncesi uygulanan alkali, alkali-asit ve kumlama yüzey işlemlerinin 7075 Alüminyum alaşımlarının aşınma davranışlarına etkileri. Gazi Üniversitesi Mühendislik Mimarlık Fakültesi Dergisi, vol.38, no.2, 2023, ss.795 - 806. 10.17341/gazimmfd.1024352
AMA Gül C,Albayrak S,ÇİNİCİ H,algan şimşek i Magnetron sıçratma ile Tantal-Oksit kaplama öncesi uygulanan alkali, alkali-asit ve kumlama yüzey işlemlerinin 7075 Alüminyum alaşımlarının aşınma davranışlarına etkileri. Gazi Üniversitesi Mühendislik Mimarlık Fakültesi Dergisi. 2023; 38(2): 795 - 806. 10.17341/gazimmfd.1024352
Vancouver Gül C,Albayrak S,ÇİNİCİ H,algan şimşek i Magnetron sıçratma ile Tantal-Oksit kaplama öncesi uygulanan alkali, alkali-asit ve kumlama yüzey işlemlerinin 7075 Alüminyum alaşımlarının aşınma davranışlarına etkileri. Gazi Üniversitesi Mühendislik Mimarlık Fakültesi Dergisi. 2023; 38(2): 795 - 806. 10.17341/gazimmfd.1024352
IEEE Gül C,Albayrak S,ÇİNİCİ H,algan şimşek i "Magnetron sıçratma ile Tantal-Oksit kaplama öncesi uygulanan alkali, alkali-asit ve kumlama yüzey işlemlerinin 7075 Alüminyum alaşımlarının aşınma davranışlarına etkileri." Gazi Üniversitesi Mühendislik Mimarlık Fakültesi Dergisi, 38, ss.795 - 806, 2023. 10.17341/gazimmfd.1024352
ISNAD Gül, Canser vd. "Magnetron sıçratma ile Tantal-Oksit kaplama öncesi uygulanan alkali, alkali-asit ve kumlama yüzey işlemlerinin 7075 Alüminyum alaşımlarının aşınma davranışlarına etkileri". Gazi Üniversitesi Mühendislik Mimarlık Fakültesi Dergisi 38/2 (2023), 795-806. https://doi.org/10.17341/gazimmfd.1024352
Sayfa Oluşturulma Tarihi
24-04-2024 6:5

İLETİŞİM

TÜBİTAK ULAKBİM TR Dizin

Yüzüncüyıl, İşçi Blokları Mahallesi

Muhsin Yazıcıoğlu Caddesi No:51/C

06530 Çankaya / ANKARA +90 (312) 298 92 00

trdizin@tubitak.gov.tr

TÜBİTAK ULAKBİM Ulusal Akademik Ağ ve Bilgi Merkezi Cahit Arf Bilgi Merkezi © Tüm Hakları Saklıdır. Gizlilik Politikası Kullanım Şartları