TRIBOCORROSION PROPERTIES OF BORIDED AND Al2O3-COATED NiTi MATERIAL

Yakup UZUN (Atatürk Üniversitesi, Mühendislik Fakültesi, Makine Mühendisliği Bölümü, Erzurum, Türkiye)
Erzincan Üniversitesi Fen Bilimleri Enstitüsü Dergisi
1 1
Yıl: 2022 Cilt: 15 Sayı: 3 Sayfa Aralığı: 873 - 884 Metin Dili: İngilizce DOI: 10.18185/erzifbed.1181562 İndeks Tarihi: 30-03-2023

TRIBOCORROSION PROPERTIES OF BORIDED AND Al2O3-COATED NiTi MATERIAL

Öz:
The purpose of this study was to investigate the tribological properties of NiTi shape-memory alloy that was borided and coated with Al2O3 using the electrophoretic deposition (EPD) method. For the study, the sample surface was borided for 1 and 4 h at 800°C with the method of pack boriding, and the surface of the sample that was borided was coated with Al2O3 using the EPD method. The tribocorrosion properties of the untreated samples, borided samples, and borided and (duplex) Al2O3-coated samples were investigated and characterized using XRD and SEM devices. Accordingly, following the boriding treatment on the NiTi material, Al2O3 coating was successfully carried out with the EPD method. In comparison to the untreated samples, the tribocorrosion resistance of the surface-treated samples under a load of 3 N in a 3.5% NaCl solution increased. Additionally, among all samples, those that were subjected to the duplex surface treatment had the best tribocorrosion properties.
Anahtar Kelime: NiTi Boriding EPD Tribocorrosion

Borlanmış ve AL2O3 Kaplı NiTi Malzemenin Tribokorozyon Özellikleri

Öz:
Bu çalışmanın amacı, borlanmış ve Elektroforetik biriktirme yöntemi (EPD) ile Al2O3 kaplanmış şekil hafızalı NiTi alaşımın tribolojik özelliklerini araştırmaktır. Araştırma için numune yüzeyi kutu borlama yöntemi ile 800 ⁰C sıcaklıkta 1ve 4 h borlama yapılmış ardından borlanmış numunelerin yüzeyi EPD yöntemi ile Al2O3 kaplanmıştır. Daha sonra işlemsiz, borlanmış ve borlanarak ardından Al2O3 (dublex) kaplanmış numunelerin tribokorozyon özellikleri araştırılmış, XRD ve SEM cihazı ile karakterize edilmiştir. NiTi malzeme üzerine yapılan borlama işleminden sonra EPD yöntemi ile Al2O3 kaplama başarılı bir şekilde gerçekleştirilmiştir. İşlemsiz numuneye göre yüzey işlemi uygulanmış numunelerin %3,5 NaCl çözeltisi içerisinde 3 N yük altında Tribokorozyon direnci artmıştır. Ayrıca dublex yüzey işlemi uygulanmış numunenin diğer numunelere göre en iyi Tribokorozyon özellikler gösterdiği sonucuna varılmıştır.
Anahtar Kelime: NiTi Borlama EPD Tribokorozyon

Belge Türü: Makale Makale Türü: Araştırma Makalesi Erişim Türü: Erişime Açık
  • [1] Kaya, E., Kaya, İ., (2020) Tool wear progression of PCD and PCBN cutting tools in high speed machining of NiTi shape memory alloy under various cutting speeds, Diamond and Related Materials, 105 107810.
  • [2] Ramaiah, K., Saikrishna, C., Bhaumik, S., (2014) Ni24. 7 Ti50.3 Pd25.0 high temperature shape memory alloy with narrow thermal hysteresis and high thermal stability, Materials & Design, 56 78–83.
  • [3] Shabalovskaya, S. A., (1996) Shape Memory Alloys for Biomedical Applications. Yoneyama, T., Miyazaki, S. (Eds.), Biocompatibility of Nitinol for biomedical applications (6 -267), Woodhead Publishing, England.
  • [4] Petrini, L., Migliavacca, F., (2011) Biomedical applications of shape memory alloys, Journal of Metallurgy, 1-15.
  • [5] Bil, C., Massey, K., Abdullah, E.J., (2013) Wing morphing control with shape memory alloy actuators, J. Intell. Mater. Syst. Struct., 24 (7) 879–898.
  • [6] Pelletier, H., Muller, D., Mille, P., Grob, J., (2002) Structural and mechanical characterisation of boron and nitrogen implanted NiTi shape memory alloy. Surface and Coatings Technology, 158–159 309-317.
  • [7] Uzun, Y., Yanıkoğlu, N., Kovacı, H., Yetim, A.F., Çelik, A., (2021) The effects of boriding on metal-ceramic bond strength of Co–Cr alloy fabricated by selective laser melting, Journal of Adhesion Science And Technology, 35(14) 1576–1591.
  • [8] Aksöz, S., Bostan, B., Kaplan, Y., (2021) An Investigation on the Effects of Boronizing Process on Microstructure and Microhardness of NiTi Alloy Produced by P/M Technique, Journal of Polytechnic, 24 (2) 539-544.
  • [9] Misra, S.K., Boccaccini, A.R., (2007) Tissue engineering using ceramics and polymers. Boccaccini, A.R., Gough J.E., (Eds.) (72), Woodhead Publishing Limited, England.
  • [10] Boccaccini, A.R., Keim, S., Ma, R., Li, Y., Zhitomirsky, I. (2010) Electrophoretic deposition of biomaterials, J. R. Soc. Interface 7 581-613.
  • [11] Bakhshandeh, S., & Amin Yavari, S. (2018) Electrophoretic deposition: A versatile tool against biomaterial associated infections, Journal of Materials Chemistry B, 6(8) 1128- 1148.
  • [12] Saji, V. S. (2021) Electrophoretic (EPD) coatings for magnesium alloys, Journal of Industrial and Engineering Chemistry, 103 358-372.
  • [13] Boccaccini, A.R. and Zhitomirsky, I. (2002) Application of electrophoretic and electrolytic deposition techniques in ceramics processing, Current Opinion in Solid State & Materials Science, 6 251-260.
  • [14] Béjar M. A., Moreno E., (2006) Abrasive wear resistance of boronized carbon and low-alloy steels, Journal of Materials Processing Technology, 173(3) 352-358.
  • [15] Uzun, Y., Kovacı, H., Yetim, A. F., Çelik, A. (2019) Effect of boronizing on the structural, mechanical and tribological properties of CoCrW dental alloy produced by selective laser melting, Industrial Lubrication and Tribology, 71(3) 348–356.
  • [16] Malinovschi, V., Marin, A., Negrea, D., Andrei, V., Coaca, E. Mihailescu, C. N., Lungu, C. P. (2018) Characterization of Al 2 O 3 /ZrO 2 composite coatings deposited on Zr-2.5Nb alloy by plasma electrolytic oxidation, Appl. Surf. Sci., 451169-179.
  • [17] Sourani, F., Raeissi, K., Enayati, M. H., Kharaziha, M., Hakimizad, A., Blugan, G., Salimijazi, H. R., (2022) Corrosion and tribocorrosion behavior of ZrO2-Al2O3 composite coatings developed by plasma electrolytic oxidation for load-bearing implants, Journal of Alloys and Compounds, 920 165856.
  • [18] Luo, Y., Wu, Y., Xiao, D., Tang, K., Huang, C., Fu, R. K. Y., Zheng, S., Chu P. K. (2019) Al2O3 coating for densification of SiC ceramics and sintering kinetics, Surf. Coat. Technol., 374 603-609.
  • [19] Zhang, B., Wang, J., Yan, F., (2018) Load-dependent tribocorrosion behaviour of nickel-aluminium bronze in artificial seawater, Corros. Sci., 131 252-263.
  • [20] Martini, C., Ceschini, L., Tarterini, F., Paillard, J.M., Curran, J.A., (2010). PEO layers obtained from mixed aluminate–phosphate baths on Ti–6Al–4V: Dry sliding behaviour and influence of a PTFE topcoat, Wear, 269 47-756.
  • [21] Karakaş, M. S., Günen, A., Çarboğa, C., Karaca, Y., Demir, M., Altınay, Y., Erdoğan, A., (2021) Microstructure, some mechanical properties and tribocorrosion wear behavior of boronized Al0.07Co1.26 Cr1.80Fe1.42Mn1.35 Ni1.10 high entropy alloy, J. Alloy. Compd., 886 161222.
  • [22] Pina, V.G., Amigó, V., Muñoz A.I. (2016) Microstructural, electrochemical and triboelectrochemical characterisation of titanium-copper biomedical alloys, Corros. Sci., 109 115-125.
  • [23] Sampaio, M., Buciumeanu, M., Henriques, B., Silva, F. S., Souza, J. C. M., Gomes J. R., (2016) Comparison between PEEK and Ti6Al4V concerning micro-scale abrasion wear on dental applications, J. Mech. Behav. Biomed. Mater., 60 212-219.
APA uzun y (2022). TRIBOCORROSION PROPERTIES OF BORIDED AND Al2O3-COATED NiTi MATERIAL. , 873 - 884. 10.18185/erzifbed.1181562
Chicago uzun yakup TRIBOCORROSION PROPERTIES OF BORIDED AND Al2O3-COATED NiTi MATERIAL. (2022): 873 - 884. 10.18185/erzifbed.1181562
MLA uzun yakup TRIBOCORROSION PROPERTIES OF BORIDED AND Al2O3-COATED NiTi MATERIAL. , 2022, ss.873 - 884. 10.18185/erzifbed.1181562
AMA uzun y TRIBOCORROSION PROPERTIES OF BORIDED AND Al2O3-COATED NiTi MATERIAL. . 2022; 873 - 884. 10.18185/erzifbed.1181562
Vancouver uzun y TRIBOCORROSION PROPERTIES OF BORIDED AND Al2O3-COATED NiTi MATERIAL. . 2022; 873 - 884. 10.18185/erzifbed.1181562
IEEE uzun y "TRIBOCORROSION PROPERTIES OF BORIDED AND Al2O3-COATED NiTi MATERIAL." , ss.873 - 884, 2022. 10.18185/erzifbed.1181562
ISNAD uzun, yakup. "TRIBOCORROSION PROPERTIES OF BORIDED AND Al2O3-COATED NiTi MATERIAL". (2022), 873-884. https://doi.org/10.18185/erzifbed.1181562
APA uzun y (2022). TRIBOCORROSION PROPERTIES OF BORIDED AND Al2O3-COATED NiTi MATERIAL. Erzincan Üniversitesi Fen Bilimleri Enstitüsü Dergisi, 15(3), 873 - 884. 10.18185/erzifbed.1181562
Chicago uzun yakup TRIBOCORROSION PROPERTIES OF BORIDED AND Al2O3-COATED NiTi MATERIAL. Erzincan Üniversitesi Fen Bilimleri Enstitüsü Dergisi 15, no.3 (2022): 873 - 884. 10.18185/erzifbed.1181562
MLA uzun yakup TRIBOCORROSION PROPERTIES OF BORIDED AND Al2O3-COATED NiTi MATERIAL. Erzincan Üniversitesi Fen Bilimleri Enstitüsü Dergisi, vol.15, no.3, 2022, ss.873 - 884. 10.18185/erzifbed.1181562
AMA uzun y TRIBOCORROSION PROPERTIES OF BORIDED AND Al2O3-COATED NiTi MATERIAL. Erzincan Üniversitesi Fen Bilimleri Enstitüsü Dergisi. 2022; 15(3): 873 - 884. 10.18185/erzifbed.1181562
Vancouver uzun y TRIBOCORROSION PROPERTIES OF BORIDED AND Al2O3-COATED NiTi MATERIAL. Erzincan Üniversitesi Fen Bilimleri Enstitüsü Dergisi. 2022; 15(3): 873 - 884. 10.18185/erzifbed.1181562
IEEE uzun y "TRIBOCORROSION PROPERTIES OF BORIDED AND Al2O3-COATED NiTi MATERIAL." Erzincan Üniversitesi Fen Bilimleri Enstitüsü Dergisi, 15, ss.873 - 884, 2022. 10.18185/erzifbed.1181562
ISNAD uzun, yakup. "TRIBOCORROSION PROPERTIES OF BORIDED AND Al2O3-COATED NiTi MATERIAL". Erzincan Üniversitesi Fen Bilimleri Enstitüsü Dergisi 15/3 (2022), 873-884. https://doi.org/10.18185/erzifbed.1181562
Sayfa Oluşturulma Tarihi
24-04-2024 20:41

İLETİŞİM

TÜBİTAK ULAKBİM TR Dizin

Yüzüncüyıl, İşçi Blokları Mahallesi

Muhsin Yazıcıoğlu Caddesi No:51/C

06530 Çankaya / ANKARA +90 (312) 298 92 00

trdizin@tubitak.gov.tr

TÜBİTAK ULAKBİM Ulusal Akademik Ağ ve Bilgi Merkezi Cahit Arf Bilgi Merkezi © Tüm Hakları Saklıdır. Gizlilik Politikası Kullanım Şartları