TY  - JOUR
TI  - The flexural strength of acrylic resin repairs reinforced with different nanoparticles
AB  - Aim: The purpose of this study is to assess the flexural strength of heat-cure acrylic resins repaired with auto-polymerized acrylic resins modified with 1%, 3% TiO2, Fe2O3, CuO nanoparticles. Materials and Methods: Fifty-six samples (65x10x2.5 mm) were prepared with heat- cure acrylic resins and divided into 7 groups (8 samples each) to make repair procedure: Specimens were repaired with unmodified (control group) and 1%, 3% TiO2, Fe2O3, CuO added auto-polymerized acrylic resins. For 3-point flexural test, the force was loaded at 5 mm/min crosshead speed directly to the middle part of the repaired acrylic resin with a Universal Testing Machine. Data were analyzed statistically by ANOVA followed by Tukey test (p < 0.05). Results: Control group showed lower strength values than the other groups. 1% TiO2 nanoparticle added group showed significantly higher flexural strength values than 3% added groups and control group (p < 0.05). The highest strength value was measured in 1% TiO2 group. Conclusion: Acrylic resins reinforced with 1% TiO2 developed higher strength than resins reinforced with 3 % TiO2, Fe2O3, CuO nanoparticles. Adding 1% nanoparticles to resins could improve the fracture strength of materials.
AU  - Ozkan Ata, Secil
AU  - AKAY, CANAN
AU  - mumcu, emre
DO  - 10.5455/annalsmedres.2022.02.080
PY  - 2022
JO  - Annals of Medical Research
VL  - 29
IS  - 10
SN  - 2636-7688
SP  - 1073
EP  - 1076
DB  - TRDizin
UR  - http://search/yayin/detay/1169274
ER  -