Effect of aging time and temperature on properties of AA7075 alloy
Yıl: 2023 Cilt: 13 Sayı: 1 Sayfa Aralığı: 23 - 31 Metin Dili: İngilizce DOI: 10.17714/gumusfenbil.1099882 İndeks Tarihi: 19-07-2023
Effect of aging time and temperature on properties of AA7075 alloy
Öz: In this study, the effect of aging at different temperatures and times on the microstructure and mechanical properties of AA7075-T6 alloy was investigated. The samples prepared for the experimental studies were subjected to solution, quenching, and then aging heat treatment at 100 ⁰C and 200 ⁰C for different periods (42-66-90 hours). The microstructure and mechanical properties of the experimental samples were investigated by hardness, compression test and scanning electron microscope (SEM). As a result of the studies, it was determined that the aging heat treatment had a positive effect on the microstructure and mechanical properties of the AA7075 alloy compared to the reference sample. Especially as a result of the heat treatments at 100 ⁰C, higher results were obtained in hardness and compression strength compared to the initial values.
Anahtar Kelime: Yaşlandırma süresinin ve sıcaklığının AA7075 alaşımının özelliklerine etkisi
Öz: Bu çalışmada, farklı sıcaklı ve sürelerde uygulanan yaşlandırma işleminin, AA7075-T6 alaşımının mikroyapı ve mekanik özelliklerine etkisi incelenmiştir. Deneysel çalışmalar için hazırlanan numuneler, çözeltiye alma, su verme, daha sonra 100 ⁰C ve 200 ⁰C sıcaklıkta farklı sürelerde (42-66-90 saat) yaşlandırma ısıl işlemine tabi tutulmuşlardır. Deneysel numunelerin, sertlik, basma deneyi ve taramalı elektron mikroskobu (SEM) ile mikroyapı ve mekanik özellikleri incelenmiştir. Yapılan çalışmalar sonucunda, yapılan yaşlandırma ısıl işleminin AA7075 alaşımının mikroyapı ve mekanik özelliklerini referans numuneye göre olumlu yönde etkilediği tespit edilmiştir. Özellikle 100 ⁰C de yapılan ısıl işlemler sonucu sertlik ve basma mukavemetinde başlangıç değerlerine göre daha yüksek sonuçlar elde edilmiştir.
Anahtar Kelime: Belge Türü: Makale Makale Türü: Araştırma Makalesi Erişim Türü: Erişime Açık
- Ak, M. (2012). AA206 alüminyum döküm alaşımında empürite demirin mekanik özelliklere etkilerinin incelenmesi [Yüksek Lisans Tezi, İstanbul Teknik Üniversitesi Fen Bilimleri Enstitüsü].
- Altuntaş, G. (2020). Al 7075 alaşımına RRA ısıl işlem ve ön deformasyon etkilerinin incelenmesi [Yüksek Lisans Tezi, Gazi Üniversitesi Fen Bilimleri Enstitüsü].
- Al-Saadi, H. I. A. & Tunay, R. F. (2017). Suni yaşlandırma işleminin alüminyum alaşımının sertliği üzerine etkisi. Mühendislik Bilimleri ve Tasarım Dergisi, 5(3), 525-532.
- Aydın, B. (2002). AA2014 Alaşımında yaşlandırma ısıl işleminin işlenebilirlik üzerindeki etkilerinin incelenmesi [Yüksek Lisans Tezi, Gazi Üniversitesi Fen Bilimleri Enstitüsü].
- Baydoğan, M., Çimenoğlu, H., & Kayali, E. S. (2004). RRA işleminin 7075 alaşımının mekanik özelliklerine etkisi. İtüdergisi/d, 3(6), 108-116.
- Budak, S. (2016). Alüminyum silisyum alaşımı bir yatak malzemesinin aşınma performansına kolemanit ilavesinin etkisinin incelenmesi/Investigation of effect of colemanite addition on the wear performance of an aluminum silicon alloy journal bearing material [Doktora Tezi, Fırat Üniversitesi Fen Bilimleri Enstitüsü].
- Chen, J., Zhen, L., Yang, S., Shao, W., & Dai, S. (2009). Investigation of precipitation behavior and related hardening in AA 7055 aluminum alloy. Materials Science and Engineering: A, 500(1-2), 34-42. https://doi.org/10.1016/j.msea.2008.09.065
- Cina, B.M., (1974). Reducing the susceptibility of alloys, particularly aluminum alloys to stress corrosion cracking, U.S. Patent, No: 3,856,584. Washington, DC: U.S. Patent and Trademark Office.
- Demirel, M. Y., & Karaağaç, İ. (2020). 7075-T6 alaşımının mikroyapı ve mekanik özelliklerine tavlama işleminin etkisinin deneysel olarak araştırılması. Politeknik Dergisi, 23(2), 283-289. https://doi.org/10.2339/politeknik.534322
- Durmuş, H., Uzun, R. O., & Şahin, S. (2011). Retrogresyon işleminin 7075 alüminyum alaşımının aşınma davranışına etkisi. 6 th International Advanced Technologies Symposium (IATS’11) (pp. 16-18), Elazığ.
- El-Amoush, A. S. (2011). Intergranular corrosion behavior of the 7075-T6 aluminum alloy under different annealing conditions. Materials Chemistry and Physics, 126(3), 607-613. https://doi.org/10.1016/j.matchemphys.2011.01.010
- Geçkinli, E. (2002). Alüminyum alaşımlarının ısıl işlemi, 2. Isıl İşlem Sempozyumu, 07-08 Şubat, İstanbul.
- Güleryüz, K., & Kaçar, R. (2011). Deformasyon yaşlanmasının AA7075 alüminyum alaşımının mekanik özelliklerine etkisinin incelenmesi. 6th International Advanced Technologies Symposium (IATS’11) (Vol. 147, p. 152), Elazığ.
- Gültekin, K., & Korkmaz, Y. (2021). AA2024-T3 alüminyum alaşımlarına uygulanan farklı yüzey hazırlama ve pürüzlülük işlemlerinin yapıştırma bağlantılarına etkisi. Gümüşhane Üniversitesi Fen Bilimleri Enstitüsü Dergisi, 11(4), 1269-1281. https://doi.org/10.17714/gumusfenbil.895318
- Hansen, V., Karlsen, O. B., Langsrud, Y., & Gjønnes, J. (2004). Precipitates, zones and transitions during aging of Al- Zn-Mg-Zr 7000 series alloy. Materials science and technology, 20(2), 185-193. https://doi.org/10.1179/026708304225010424
- Kalyon, A., & Özyürek, D. (2017). Investigation of the effect of different heat treatments on wear behavior of AA7075 alloy. Acta Physica Polonica A, 131(1), 150-152.
- Karaaslan, A., Kaya, I., & Atapek, H. (2007). Effect of aging temperature and of retrogression treatment time on the microstructure and mechanical properties of alloy AA 7075. Metal Science and Heat Treatment, 49(9), 443-447.
- Kibar, E. (2010). 7075 alüminyum alaşımlarına uygulanan RRA ısıl işlemlerinin mikroyapı ve mekanik özelliklere etkisi [Yüksek Lisans Tezi, Sakarya Üniversitesi Fen Bilimleri Enstitüsü].
- Li, R., Liu, T., Su, R., & Qu, Y. (2018). Microstructure and mechanical properties of spray-formed 7075 alloy during retrogression. Journal of Materials Engineering and Performance, 27(9), 4437-4443. https://doi.org/10.1007/s11665-018-3606-1
- Naeem, H. T., & Mohammed, K. S. (2013). Retrogression and re-aging of aluminum alloys (AA 7075) containing nickel. Digest Journal of Nanomaterials & Biostructures (DJNB), 8(4).
- Özer, G., & Karaaslan, A. (2017). Properties of AA7075 aluminum alloy in aging and retrogression and reaging process. Transactions of Nonferrous Metals Society of China, 27(11), 2357-2362. https://doi.org/10.1016/S1003- 6326(17)60261-9
- Özyürek, D., Yilmaz, R., & Kibar, E. (2012). RRA işleminde yeniden çözeltiye alma parametrelerin 7075 alüminyum alaşimlarinin çekme dayanimina etkisi. Gazi Üniversitesi Mühendislik Mimarlık Fakültesi Dergisi, 27(1), 193- 203.
- Rokni, M. R., Widener, C. A., Champagne, V. K., Crawford, G. A., & Nutt, S. R. (2017). The effects of heat treatment on 7075 Al cold spray deposits. Surface and Coatings Technology, 310, 278-285. https://doi.org/10.1016/j.surfcoat.2016.10.064
- Şenel, M. C. (2020). Toz metalürjisi yöntemiyle üretilen saf Al ve Al-B4C, Al-Al2O3 kompozitlerin mekanik ve mikroyapı özelliklerinin karşılaştırılması. Gümüşhane Üniversitesi Fen Bilimleri Enstitüsü Dergisi, 10(3), 783- 795. https://doi.org/10.17714/gumusfenbil.689359
- Şenel, M. C., & Gürbüz, M. (2020). Mikron altı boyutlu alümina katkısının ve soğuk deformasyon işleminin üretilen alüminyum kompozit yapının mekanik özellikleri ve mikroyapısına etkisi. Gümüşhane Üniversitesi Fen Bilimleri Enstitüsü Dergisi, 10(1), 76-85. https://doi.org/10.17714/gumusfenbil.528780
- Şimşek, İ., Yıldırım, M., Özyürek, D., & Tunçay, T. (2018). AA7075 alaşımının T6 ısıl işleminde yaşlandırma süresinin aşınma davranışı üzerine etkisi. İleri Teknoloji Bilimleri Dergisi, 7(1), 42-49.
- Xiao, Y. P., Pan, Q. L., Li, W. B., Liu, X. Y., & He, Y. B. (2011). Influence of retrogression and re-aging treatment on corrosion behaviour of an Al–Zn–Mg–Cu alloy. Materials & Design, 32(4), 2149-2156. https://doi.org/10.1016/j.matdes.2010.11.036
- Yilmaz, R., Özyürek, D., & Kibar, E. (2012). Yeniden çözeltiye alma parametrelerinin 7075 alüminyum alaşımlarının sertlik ve aşınma davranışlarına etkisi. Gazi Üniversitesi Mühendislik Mimarlık Fakültesi Dergisi, 27(2), 429- 438.
| APA | Budak S, ÇOLAK H, YAKUT Y (2023). Effect of aging time and temperature on properties of AA7075 alloy. , 23 - 31. 10.17714/gumusfenbil.1099882 |
| Chicago | Budak Selahattin,ÇOLAK HARUN,YAKUT YUSUF Effect of aging time and temperature on properties of AA7075 alloy. (2023): 23 - 31. 10.17714/gumusfenbil.1099882 |
| MLA | Budak Selahattin,ÇOLAK HARUN,YAKUT YUSUF Effect of aging time and temperature on properties of AA7075 alloy. , 2023, ss.23 - 31. 10.17714/gumusfenbil.1099882 |
| AMA | Budak S,ÇOLAK H,YAKUT Y Effect of aging time and temperature on properties of AA7075 alloy. . 2023; 23 - 31. 10.17714/gumusfenbil.1099882 |
| Vancouver | Budak S,ÇOLAK H,YAKUT Y Effect of aging time and temperature on properties of AA7075 alloy. . 2023; 23 - 31. 10.17714/gumusfenbil.1099882 |
| IEEE | Budak S,ÇOLAK H,YAKUT Y "Effect of aging time and temperature on properties of AA7075 alloy." , ss.23 - 31, 2023. 10.17714/gumusfenbil.1099882 |
| ISNAD | Budak, Selahattin vd. "Effect of aging time and temperature on properties of AA7075 alloy". (2023), 23-31. https://doi.org/10.17714/gumusfenbil.1099882 |
| APA | Budak S, ÇOLAK H, YAKUT Y (2023). Effect of aging time and temperature on properties of AA7075 alloy. Gümüşhane Üniversitesi Fen Bilimleri Dergisi, 13(1), 23 - 31. 10.17714/gumusfenbil.1099882 |
| Chicago | Budak Selahattin,ÇOLAK HARUN,YAKUT YUSUF Effect of aging time and temperature on properties of AA7075 alloy. Gümüşhane Üniversitesi Fen Bilimleri Dergisi 13, no.1 (2023): 23 - 31. 10.17714/gumusfenbil.1099882 |
| MLA | Budak Selahattin,ÇOLAK HARUN,YAKUT YUSUF Effect of aging time and temperature on properties of AA7075 alloy. Gümüşhane Üniversitesi Fen Bilimleri Dergisi, vol.13, no.1, 2023, ss.23 - 31. 10.17714/gumusfenbil.1099882 |
| AMA | Budak S,ÇOLAK H,YAKUT Y Effect of aging time and temperature on properties of AA7075 alloy. Gümüşhane Üniversitesi Fen Bilimleri Dergisi. 2023; 13(1): 23 - 31. 10.17714/gumusfenbil.1099882 |
| Vancouver | Budak S,ÇOLAK H,YAKUT Y Effect of aging time and temperature on properties of AA7075 alloy. Gümüşhane Üniversitesi Fen Bilimleri Dergisi. 2023; 13(1): 23 - 31. 10.17714/gumusfenbil.1099882 |
| IEEE | Budak S,ÇOLAK H,YAKUT Y "Effect of aging time and temperature on properties of AA7075 alloy." Gümüşhane Üniversitesi Fen Bilimleri Dergisi, 13, ss.23 - 31, 2023. 10.17714/gumusfenbil.1099882 |
| ISNAD | Budak, Selahattin vd. "Effect of aging time and temperature on properties of AA7075 alloy". Gümüşhane Üniversitesi Fen Bilimleri Dergisi 13/1 (2023), 23-31. https://doi.org/10.17714/gumusfenbil.1099882 |