Study on Electrical, Thermal, Magnetic Properties and Microstructure for - Al, -Al2Cu, ω-Al7Cu2Fe Phases in Al-32.5 wt. % Cu-1 wt. % Fe Ternary Alloy

Canan ALPER BİLLUR, (Sivas Cumhuriyet Üniversitesi, Sivas Teknik Bilimler Meslek Yüksekokulu, Sivas, Türkiye)
Buket SAATÇİ (Erciyes Üniversitesi, Fizik Bölümü, Kayseri, Türkiye)
Cumhuriyet Science Journal
0 0
Yıl: 2023 Cilt: 44 Sayı: 4 Sayfa Aralığı: 785 - 792 Metin Dili: İngilizce DOI: 10.17776/csj.1349226 İndeks Tarihi: 03-01-2024

Study on Electrical, Thermal, Magnetic Properties and Microstructure for - Al, -Al2Cu, ω-Al7Cu2Fe Phases in Al-32.5 wt. % Cu-1 wt. % Fe Ternary Alloy

Öz:
The electrical properties of the Al-32.5 wt. % Cu-1 wt. % Fe ternary alloy were examined, it was observed that the electrical resistivity increased depending on the temperature and it was found as 6.8546x10-8 Ωm - 5.7780x10-7Ωm in the temperature range of 298-810K. The thermal conductivity was calculated using electrical measurement results and it was observed that it decreased depending on the temperature. The ternary alloy (cubic -Al, Fm-3m, 225 a = 4.0480 Å, -tetragonal Al2Cu, I4mcm, 140, a=6.0654 Å c=4.8732 Å, ω-tetragonal Al7Cu2Fe, P4 /mnc, 128, a = 6.3360 Å, m and c = 14.87 Å) phases were obtained. In this ternary alloy, phases were clearly seen in XRD studies and EDAX analyzes at room temperature. Magnetic properties such as magnetic transition temperature and magnetization curves of the alloy were determined.
Anahtar Kelime: Mechanical Properties Electrical Properties Thermal Properties Magnetic Properties Intermetallic Phase

Belge Türü: Makale Makale Türü: Araştırma Makalesi Erişim Türü: Erişime Açık
  • [1] Travessa D.N., Cardoso K.R.,Wolf W., Jr. Jorge A.M., Botta W.J., The Formation of Quasicrystal Phase inn Al-Cu-Fe System by Mechanical Alloying Materials Research, 15 (5) ( 2012) 749-752.
  • [2] Školáková A., Novák P., Mejzliková L., Prŭsa F., Salvetr P., Vojtěch D., Structure and Mechanical Properties of Al-Cu-Fe-X Alloys with Excellent Thermal Stability, Materials (Basel) NOV., 10 (11) (2017) 1269.
  • [3] Huttunen-Saarivirta E., Microstructure, fabrication and properties of quasicrystalline Al–Cu–Fe alloys: A review., J. Alloy. Compd., 363 (2004) 154–178.
  • [4] Biswas K., and Chattopadhyay K., Formation of w-Al7Cu2Fe phase during laser processing of quasicrystal-forming Al-Cu-Fe alloy, Philosophical Magazine Letters, 88 3 (2008) 219-230.
  • [5] Tsai A.P., Inoue A. and Masumoto T., A.Stable Quasicrystal in Al-Cu-Fe System, Jap. J. appl. Phys., 26 (9) (1987) L1505-L1507.
  • [6] Liu W. and Köster U., Decomposition of the icosahedral phase in AlCuFe alloys, Mater. Sci. Engng A, 133 (1991) 388-392.
  • [7] Gayle F.W., Shapiro A.J., Boancaniello F.S., et al., The Al-Cu-Fe phase diagram: 0 to 25 At. pct Fe and 50 to 75 At. Pct Al — Equilibria Involving the Icosahedral Phase, Metall. Trans. A, 23 (1992) 2409-2417.
  • [8] Gratias D., Calvayrac Y., Devaud-Rzepski J., et al., Phase diagram and structures of the ternary AlCuFe system in the vicinity of the icosahedral region, J. Non-Crystalline Solids 153–154 (1993) 482-488.
  • [9] Grushko B., Wittenberg R. and Holland-Moritz D., Solidification of Al–Cu–Fe alloys forming icosahedral phase, J. Mater. Res, 11 (1996) 2177-2185.
  • [10] Gui J., Wang J., Wang R., et al., On some discrepancies in the literature about the formation of icosahedral quasi-crystal in Al–Cu–Fe alloys, J. Mater. Res, 16 (2001) 1037-1046.
  • [11] Rosas G. and Perez R., On the transformations of the ψ-AlCuFe icosahedral phase, Mater. Lett, 47 (2001) 225-230.
  • [12] Zhang L. and Lück R., Z., Phase diagram of the Al–Cu–Fe quasicrystal-forming alloy system, Metallkd, 94 (2003) 91-97.
  • [13] Auderbert F., Colaço R., Viller R., et al., Laser cladding of aluminium-base quasicrystalline alloys, Scripta Mater, 40 (1999) 551-557.
  • [14] Biswas K., Galun R., Mordike B.L., et al., Laser cladding of quasicrystal forming Al–Cu–Fe on aluminum, J. Non-Crystalline Solids, 334–335 (2004) 517.
  • [15] Zahoor A., Nawaz Shahid R., Tariq N.H., Wahab H., Anwar S., Rafiq M.A., Ameer A., Izhar S., Ali F., Hasan B.A., Effect on electrical and magnetic behavior of Al-Cu-Fe quasicrystals during surface leaching, Applied Physics A, (2021) 127, 551.
  • [16] Yin S, Xie Z, Bian Q, He B, Pan Z, Sun Z et al., Formation of AlCuFe icosahedral quasicrystal by mechanical alloying: XAFS and XRD studies. Journal of Alloys and Compounds, 455 (1-2) (2008) 314-321.
  • [17] Willey L.A., Metallography, Structures and Phase Diagrams, Vol.8, Metals Handbook 8th ed., American Society for Metals, Metals Park, OH. (1973)
  • [18] Prevarskiy A.P., Investigation of Fe-Cu-Al Alloys, Russ. Metall. TR:Izv.Akad. Nauk SSSR, Metall., 4 (1971) 154-156.
  • [19] Yuan G.C., Influence of silicon content on friction and wear characteristics of new Al-Sn-Si alloys, Chin. J. Nonferrous Metals, 8 (9) (1998) 101-105.
  • [20]Rudnev V., Loveless D., Cook R., Black M., Handbook of Induction Heating. Markel Dekker Inc, New York, (2003) 119-120.
  • [21] Ari M., Saatçi B., Gündüz M., Payveren M., Durmus S., Thermo-electrical characterization of Sn-Zn alloys, Mater. Char., 59 (2008) 757-763.
  • [22] Zhou D.J., Study on Al-Sn-Si-Cu bearing alloy, J. Light Alloy Fabr. Technol., 28 (5) (2000) 44-46.
  • [23]Yamasue, E., Susa, M., Fukuyama, H., Nagata, K., Deviation from Wiedemann-Franz law for the thermal conductivity of liquid tin and lead at elevated temperature., Int. J. Thermophys. 24 (2003) 713-730.
  • [24]Sergent, E.J., Krum, A., Thermal management handbook: for electronic assemblies. 1 edition, McGraw-Hill Professional: New York, (1998) 26.
  • [25]Bandyopadhyay, A. Dutta, Thermal, optical and dielectric properties of phase stabilized δ – Dy–Bi2O3 ionic conductors, J. Phys. Chem. Solids, 102 (2015) 12–20.
  • [26]Böyük U., Maraşlı N., Çadırlı E., Kaya H., Keşlioğlu K., Variations of microhardness with solidification parameters and electrical resistivity with temperature for Al-Cu-Ag eutecitc alloy., Current Applied Physics 12 (2012) 7-10.
  • [27] Kaya H., Dependence of electrical resistivity ontemperature and composition of Al–Cu alloys, Materials Research Innovations, 16 (3) (2012) 224-229.
  • [28]Çadırlı E., Böyük U., Engin S., Kaya H., Effect of silicon on microstructure, mechanical and electrical properties of the directionally solidified Al-based quaternary alloys, J. Alloys and Comp., 694 (2017) 471-479.
  • [29]Youjun Z., Mingqiang H., Guangtao L., Chengwei Z., Vitali P.B., Eran G., Yingwei F., Jung-Fu L., Reconciliation of experiments and theory on transport properties of iron and the geodynamo. Phys. Rev. Lett 125 (2020) 0.78501.
  • [30]Touloukian Y.S., Powell R.W., Ho C.Y., Klemens P.G., Thermal Conductivity Metallic Elements and Alloys, vol. 1, New York, Washington, (1970) 60.
  • [31] Choi S.W.,Cho H.S. ,Kumai S., Effect of the precipitation of secondary phases on the thermal diffusivity and thermal conductivitiy of Al-4.5 Cu alloy, J.Alloys and Comp. 688 (2016) 897-902.
  • [32]Nguyen H. V. , Do N. B. , Nguyen T. H. O. , Nguyen C. S. , Trinh V. T. , Le H. T., Junior A. M. J., Synthesis and magnetic properties of Al–Cu–Fe quasicrystals prepared by mechanical alloying and heat treatment, J. of Materials Research, 38 (2023) 3 644-653.
  • [33]Oanha N. T. H., Vieta N. H., Dudina D. V., Jorge Jr A. M., Kimi Ji-Soon, Structural characterization and magnetic properties of Al82Fe16TM2 (TM: Ti, Ni, Cu) alloys prepared by mechanical alloying, J. of Non-Crystalline Solids, 468 (2017) 67-73.
  • [34]Li Z., Bai H. Y., Pan M. X., Zhao De Q., Wang W. L., Wang W. H., Formation, properties, thermal characteristics, and crystallization of hard magnetic Pr–Al–Fe–Cu bulk metallic glasses, J. Mater. Res., Vol. 18 (2003) 9 2208-2213.
APA alper billur c, SAATÇI B (2023). Study on Electrical, Thermal, Magnetic Properties and Microstructure for - Al, -Al2Cu, ω-Al7Cu2Fe Phases in Al-32.5 wt. % Cu-1 wt. % Fe Ternary Alloy. , 785 - 792. 10.17776/csj.1349226
Chicago alper billur canan,SAATÇI BUKET Study on Electrical, Thermal, Magnetic Properties and Microstructure for - Al, -Al2Cu, ω-Al7Cu2Fe Phases in Al-32.5 wt. % Cu-1 wt. % Fe Ternary Alloy. (2023): 785 - 792. 10.17776/csj.1349226
MLA alper billur canan,SAATÇI BUKET Study on Electrical, Thermal, Magnetic Properties and Microstructure for - Al, -Al2Cu, ω-Al7Cu2Fe Phases in Al-32.5 wt. % Cu-1 wt. % Fe Ternary Alloy. , 2023, ss.785 - 792. 10.17776/csj.1349226
AMA alper billur c,SAATÇI B Study on Electrical, Thermal, Magnetic Properties and Microstructure for - Al, -Al2Cu, ω-Al7Cu2Fe Phases in Al-32.5 wt. % Cu-1 wt. % Fe Ternary Alloy. . 2023; 785 - 792. 10.17776/csj.1349226
Vancouver alper billur c,SAATÇI B Study on Electrical, Thermal, Magnetic Properties and Microstructure for - Al, -Al2Cu, ω-Al7Cu2Fe Phases in Al-32.5 wt. % Cu-1 wt. % Fe Ternary Alloy. . 2023; 785 - 792. 10.17776/csj.1349226
IEEE alper billur c,SAATÇI B "Study on Electrical, Thermal, Magnetic Properties and Microstructure for - Al, -Al2Cu, ω-Al7Cu2Fe Phases in Al-32.5 wt. % Cu-1 wt. % Fe Ternary Alloy." , ss.785 - 792, 2023. 10.17776/csj.1349226
ISNAD alper billur, canan - SAATÇI, BUKET. "Study on Electrical, Thermal, Magnetic Properties and Microstructure for - Al, -Al2Cu, ω-Al7Cu2Fe Phases in Al-32.5 wt. % Cu-1 wt. % Fe Ternary Alloy". (2023), 785-792. https://doi.org/10.17776/csj.1349226
APA alper billur c, SAATÇI B (2023). Study on Electrical, Thermal, Magnetic Properties and Microstructure for - Al, -Al2Cu, ω-Al7Cu2Fe Phases in Al-32.5 wt. % Cu-1 wt. % Fe Ternary Alloy. Cumhuriyet Science Journal, 44(4), 785 - 792. 10.17776/csj.1349226
Chicago alper billur canan,SAATÇI BUKET Study on Electrical, Thermal, Magnetic Properties and Microstructure for - Al, -Al2Cu, ω-Al7Cu2Fe Phases in Al-32.5 wt. % Cu-1 wt. % Fe Ternary Alloy. Cumhuriyet Science Journal 44, no.4 (2023): 785 - 792. 10.17776/csj.1349226
MLA alper billur canan,SAATÇI BUKET Study on Electrical, Thermal, Magnetic Properties and Microstructure for - Al, -Al2Cu, ω-Al7Cu2Fe Phases in Al-32.5 wt. % Cu-1 wt. % Fe Ternary Alloy. Cumhuriyet Science Journal, vol.44, no.4, 2023, ss.785 - 792. 10.17776/csj.1349226
AMA alper billur c,SAATÇI B Study on Electrical, Thermal, Magnetic Properties and Microstructure for - Al, -Al2Cu, ω-Al7Cu2Fe Phases in Al-32.5 wt. % Cu-1 wt. % Fe Ternary Alloy. Cumhuriyet Science Journal. 2023; 44(4): 785 - 792. 10.17776/csj.1349226
Vancouver alper billur c,SAATÇI B Study on Electrical, Thermal, Magnetic Properties and Microstructure for - Al, -Al2Cu, ω-Al7Cu2Fe Phases in Al-32.5 wt. % Cu-1 wt. % Fe Ternary Alloy. Cumhuriyet Science Journal. 2023; 44(4): 785 - 792. 10.17776/csj.1349226
IEEE alper billur c,SAATÇI B "Study on Electrical, Thermal, Magnetic Properties and Microstructure for - Al, -Al2Cu, ω-Al7Cu2Fe Phases in Al-32.5 wt. % Cu-1 wt. % Fe Ternary Alloy." Cumhuriyet Science Journal, 44, ss.785 - 792, 2023. 10.17776/csj.1349226
ISNAD alper billur, canan - SAATÇI, BUKET. "Study on Electrical, Thermal, Magnetic Properties and Microstructure for - Al, -Al2Cu, ω-Al7Cu2Fe Phases in Al-32.5 wt. % Cu-1 wt. % Fe Ternary Alloy". Cumhuriyet Science Journal 44/4 (2023), 785-792. https://doi.org/10.17776/csj.1349226
Sayfa Oluşturulma Tarihi
24-04-2024 18:49

İLETİŞİM

TÜBİTAK ULAKBİM TR Dizin

Yüzüncüyıl, İşçi Blokları Mahallesi

Muhsin Yazıcıoğlu Caddesi No:51/C

06530 Çankaya / ANKARA +90 (312) 298 92 00

trdizin@tubitak.gov.tr

TÜBİTAK ULAKBİM Ulusal Akademik Ağ ve Bilgi Merkezi Cahit Arf Bilgi Merkezi © Tüm Hakları Saklıdır. Gizlilik Politikası Kullanım Şartları