Color Stability of NeoMTA Plus and MTA Plus when Mixed with Anti-washout Gel or Distilled Water

Öz:
Objective: This study aims to evaluate the effect of the special anti-washout gel mixing agent on the color stability of mineral trioxide aggregate (MTA) Plus and NeoMTA Plus in contact with distilled water, ethylenediaminetetraacetic acid (EDTA) and sodium hypochlorite (NaOCl). Materials and Methods: One set of three specimens was mixed using the antiwashout gel and the other set of three specimens was mixed using distilled water. Then, one specimen from each group was immersed in distilled water, 5% NaOCl or EDTA solutions for 24 hours. The color change of each specimen was assessed using spectrophotometer. The data were evaluated statistically with two-way ANOVA and post-hoc Tukey tests. Results: It was found that there was no statistically significant differences among the color changes of the MTA Plus and NeoMTA Plus mixed with either distilled water or gel when immersed in distilled water and EDTA (p>0.05). Immersion to NaOCl resulted in the highest discoloration in all materials compared to their immersion to distilled water and EDTA. MTA Plus mixed with distilled water showed significantly greatest discoloration after contact with NaOCl (p<0.05). MTA Plus mixed with gel showed the highest color stability regardless of the solution type. Conclusion: Mixing with MTA Plus and NeoMTA Plus powder with the special antiwashout gel within their kits contributes to the color stability of the materials.
Anahtar Kelime:

Konular: Tıbbi Araştırmalar Deneysel Genel ve Dahili Tıp Diş Hekimliği Cerrahi

Çözünmeye Dirençli Jel veya Distile Suyla Hazırlanan NeoMTA Plus ve MTA Plus Materyallerinin Renk Stabilitelerinin Değerlendirilmesi

Öz:
Amaç: Bu çalışma, özel çözünme direnci sağlayan jel karıştırma ajanlarının mineral trioksit agregat (MTA) Plus ve NeoMTA Plusın renk stabilitelerine etkisini materyallerin distile su, etilendiamintetraasetik asit (EDTA) ve sodium hipoklorit (NaOCl) temasları sonrası değerlendirmeyi amaçlamaktadır. Gereç ve Yöntemler: Her iki materyalden üç numune içeren bir set çözünmeye dirençli jel kullanılarak, diğer set ise distile su kullanılarak hazırlandı. Daha sonra, her setten birer numune 24 saat boyunca distile su, %5’lik NaOCl veya EDTA solüsyonları içerisinde tutuldu. Her materyalde meydana gelen renk değişikliği pektrofotometre kullanılarak değerlendirildi. Veriler iki-yönlü ANOVA ve post-hoc Tukey testleri kullanılarak istatistiksel olarak değerlendirildi. Bulgular: MTA Plus ve NeoMTA Plus materyalleri jelle veya distile suyla karıştırılıp hazırlandıklarında distile su ve EDTA ile temasları sonucu meydana gelen renk değişiklikleri arasında istatistiksel olarak anlamlı fark olmadığı bulundu (p>0,05). NaOCl da bekletilen örneklerin tamamında distile su ve EDTA içinde bekletilen örneklere kıyasla yüksek renklenme görüldü. Distile su ile hazırlanan MTA Plus, NaOCl ile temas sonrası en yüksek renk değişimini gösterdi (p<0,05). Jel ile karıştırılan MTA Plus bekletildiği solüsyon tipinden bağımsız olarak en yüksek renk stabilitesini gösterdi. Sonuç: MTA Plus ve NeoMTA Plus tozlarının ürün kitlerindeki özel çözünme engelleyici jelle karıştırılmaları materyallerin renk stabilitelerine katkı sağlamaktadır.
Anahtar Kelime:

Konular: Tıbbi Araştırmalar Deneysel Genel ve Dahili Tıp Diş Hekimliği Cerrahi
Belge Türü: Makale Makale Türü: Araştırma Makalesi Erişim Türü: Erişime Açık
  • Van der Burgt T, Mullaney T, Plasschaert A. Tooth discoloration induced by endodontic sealers. Oral Surg Oral Med Oral Pathol 1986; 61: 84-9.
  • Davis MC, Walton RE, Rivera EM. Sealer distribution in coronal dentin. J Endod 2002; 28: 464-6.
  • Torabinejad M, White DJ. Tooth filling material and method of use. In.: Google Patents; 1995.
  • Torabinejad M, Chivian N. Clinical applications of mineral trioxide aggregate. J Endod 1999; 25: 197-205.
  • Chen MH, Chen KL, Chen CA, Tayebaty F, Rosenberg P, Lin L. Responses of immature permanent teeth with infected necrotic pulp tissue and apical periodontitis/abscess to revascularization procedures. Int Endod J 2012; 45: 294-305.
  • . Antunes Bortoluzzi E, Sivieri Araújo G, Maria Guerreiro Tanomaru J, Tanomaru-Filho M. Marginal gingiva discoloration by gray MTA: a case report. J Endod 2007; 33: 325-7.
  • Karabucak B, Li D, Lim J, Iqbal M. Vital pulp therapy with mineral trioxide aggregate. Dent Traumatol 2005;21:240-3.
  • Glickman GN, Koch KA. 21st-century endodontics. JADA 2000; 131: 39-46.
  • Watts JD, Holt DM, Beeson TJ, Kirkpatrick TC, Rutledge RE. Effects of pH and mixing agents on the temporal setting of toothcolored and gray mineral trioxide aggregate. J Endod 2007; 33: 970-3.
  • Jacobovitz M, De Lima R. Treatment of inflammatory internal root resorption with mineral trioxide aggregate: a case report. Int Endod J 2008; 41: 905-12.
  • Jacobovitz M, De Pontes Lima RK. The use of calcium hydroxide and mineral trioxide aggregate on apexification of a replanted tooth: a case report. Dent Traumatol 2009; 25: 32-6.
  • Camilleri J, Formosa L, Damidot D. The setting characteristics of MTA Plus in different environmental conditions. Int Endod J 2013; 46: 831-40.
  • Khokhar Z, Razzoog M, Yaman P. Color stability of restorative resins. Quintessence Int 1991; 22-5.
  • . Gutiérrez JH, Guzmán M. Tooth discoloration in endodontic procedures. Oral Surg Oral Med Oral Pathol 1968; 26: 706-11.
  • Ioannidis K, Mistakidis I, Beltes P, Karagiannis V. Spectrophotometric analysis of coronal discolouration induced by grey and white MTA. Int Endod J 2013; 46: 137-44.
  • Sproull RC. Color matching in dentistry. Part II. Practical applications of the organization of color. J Prost Dent 1973; 29: 556-66.
  • Camilleri J. Color stability of white mineral trioxide aggregate in contact with hypochlorite solution. J Endod 2014; 40: 436-40.
  • Keskin C, Demiryurek EO, Ozyurek T. Color stabilities of calcium silicate–based materials in contact with different irrigation solutions. J Endod 2015; 41: 409-11.
  • Felman D, Parashos P. Coronal tooth discoloration and white mineral trioxide aggregate. J Endod 2013; 39: 484-7.
  • Vallés M, Mercadé M, Duran-Sindreu F, Bourdelande JL, Roig M. Influence of light and oxygen on the color stability of five calcium silicate–based materials. J Endod 2013; 39: 525-8.
  • Kang SH, Shin YS, Lee HS, Kim SO, Shin Y, Jung IY, et al. Color changes of teeth after treatment with various mineral trioxide aggregate–based materials: an ex vivo study. J Endod 2015; 41: 737-41.
  • . Camilleri J. Staining potential of Neo MTA Plus, MTA Plus, and Biodentine used for pulpotomy procedures. J Endod 2015; 41: 1139-45.
  • Gandolfi MG, Siboni F, Primus CM, Prati C. Ion release, porosity, solubility, and bioactivity of MTA Plus tricalcium silicate. J Endod 2014; 40: 1632-7.
  • Yoldaş SE, Bani M, Atabek D, Bodur H. Comparison of the Potential Discoloration Effect of Bioaggregate, Biodentine, and White Mineral Trioxide Aggregate on Bovine Teeth: In Vitro Research. J Endod 2016; 42: 1815-8.
  • Akbari M, Rouhani A, Samiee S, Jafarzadeh H. Effect of dentin bonding agent on the prevention of tooth discoloration produced by mineral trioxide aggregate. Int J Dent 2012; 2012: 563203.
  • Belobrov I, Parashos P. Treatment of tooth discoloration after the use of white mineral trioxide aggregate. J Endod 2011; 37: 1017-20.
APA KESKİN C, SARIYILMAZ E (2018). Color Stability of NeoMTA Plus and MTA Plus when Mixed with Anti-washout Gel or Distilled Water. , 296 - 301. 10.4274/meandros.60362
Chicago KESKİN Cangül,SARIYILMAZ EVREN Color Stability of NeoMTA Plus and MTA Plus when Mixed with Anti-washout Gel or Distilled Water. (2018): 296 - 301. 10.4274/meandros.60362
MLA KESKİN Cangül,SARIYILMAZ EVREN Color Stability of NeoMTA Plus and MTA Plus when Mixed with Anti-washout Gel or Distilled Water. , 2018, ss.296 - 301. 10.4274/meandros.60362
AMA KESKİN C,SARIYILMAZ E Color Stability of NeoMTA Plus and MTA Plus when Mixed with Anti-washout Gel or Distilled Water. . 2018; 296 - 301. 10.4274/meandros.60362
Vancouver KESKİN C,SARIYILMAZ E Color Stability of NeoMTA Plus and MTA Plus when Mixed with Anti-washout Gel or Distilled Water. . 2018; 296 - 301. 10.4274/meandros.60362
IEEE KESKİN C,SARIYILMAZ E "Color Stability of NeoMTA Plus and MTA Plus when Mixed with Anti-washout Gel or Distilled Water." , ss.296 - 301, 2018. 10.4274/meandros.60362
ISNAD KESKİN, Cangül - SARIYILMAZ, EVREN. "Color Stability of NeoMTA Plus and MTA Plus when Mixed with Anti-washout Gel or Distilled Water". (2018), 296-301. https://doi.org/10.4274/meandros.60362
APA KESKİN C, SARIYILMAZ E (2018). Color Stability of NeoMTA Plus and MTA Plus when Mixed with Anti-washout Gel or Distilled Water. Meandros Medical And Dental Journal, 19(4), 296 - 301. 10.4274/meandros.60362
Chicago KESKİN Cangül,SARIYILMAZ EVREN Color Stability of NeoMTA Plus and MTA Plus when Mixed with Anti-washout Gel or Distilled Water. Meandros Medical And Dental Journal 19, no.4 (2018): 296 - 301. 10.4274/meandros.60362
MLA KESKİN Cangül,SARIYILMAZ EVREN Color Stability of NeoMTA Plus and MTA Plus when Mixed with Anti-washout Gel or Distilled Water. Meandros Medical And Dental Journal, vol.19, no.4, 2018, ss.296 - 301. 10.4274/meandros.60362
AMA KESKİN C,SARIYILMAZ E Color Stability of NeoMTA Plus and MTA Plus when Mixed with Anti-washout Gel or Distilled Water. Meandros Medical And Dental Journal. 2018; 19(4): 296 - 301. 10.4274/meandros.60362
Vancouver KESKİN C,SARIYILMAZ E Color Stability of NeoMTA Plus and MTA Plus when Mixed with Anti-washout Gel or Distilled Water. Meandros Medical And Dental Journal. 2018; 19(4): 296 - 301. 10.4274/meandros.60362
IEEE KESKİN C,SARIYILMAZ E "Color Stability of NeoMTA Plus and MTA Plus when Mixed with Anti-washout Gel or Distilled Water." Meandros Medical And Dental Journal, 19, ss.296 - 301, 2018. 10.4274/meandros.60362
ISNAD KESKİN, Cangül - SARIYILMAZ, EVREN. "Color Stability of NeoMTA Plus and MTA Plus when Mixed with Anti-washout Gel or Distilled Water". Meandros Medical And Dental Journal 19/4 (2018), 296-301. https://doi.org/10.4274/meandros.60362