Fracture surface investigations of API pipes welded with parameters determined by Taguchi method
Öz: In this study, SEM images of the samples taken from welded nick break tests of API 5L X65 pipe joints,whose welding parameters were determined by Taguchi method, were examined. As a result of theinvestigations, the elongations and orientations exhibited by the grains showed that ductile and brittlefractures were observed in the welded joints. As it was observed from equiaxed, honeycomb like imagesthat the fractures exhibited a ductile behavior. Brittle fractures that occurred due to cleavage breaks in someregions were detected. An apparent effect of welding direction was observed in fracture behavior. It wasdetected from the SEM images that a ductile fracture structure had occurred in all joints that were performedfrom bottom to top, while it was observed in the joints performed from top to bottom that generally cleavageplanes had developed along with fibrous structures in places, therefore brittle fractures had occurred.
Anahtar Kelime: Belge Türü: Makale Makale Türü: Araştırma Makalesi Erişim Türü: Erişime Açık
- F. Umbach,“Global energy security and the implications for the EU,” Energy Policy, 38, 1229–1240, 2010.
- H. Ada, S. Aksöz, T. Fındık, C. Çetinkaya, and M. Gülsün, “Tozaltı kaynak yöntemiyle birleştirilen petrol ve doğalgaz borularının mikroyapı ve mekanik özelliklerinin incelenmesi,” Politeknik Dergisi, 19 (3), 275-282, 2016.
- H. Ada, S. Aksöz, T. Fındık, C. Çetinkaya, B. Bostan and İ. Candan, “API 5L X65 Çeliklerinin MAG Kaynak Yöntemi ile Birleştirilmesinde, Kaynak İşleminin Mikroyapı ve Mekanik Özelliklere Etkisinin İncelenmesi,” Çukurova University Journal of the Faculty of Engineering and Architecture, 31, (ÖS 1), 1- 9, 2016.
- API Specifications 5L, “Specifications for Line Pipe”. 45th Edition, American Petroleum Institute, USA, 2012.
- S.H. Hashemi, "Strength - hardness statistical correlation in API X65 steel,” Mater. Sci. Eng. A, 528, 1648–1655, 2011.
- M. Rakhshkhorshid, S.H. Hashemi, “Experimental study of hot deformation behavior in API X65 steel,” Materials Science & Engineering A, 573, 37–44, 2013.
- S.H. Hashemi, D. Mohammadyani, “Characterization of weldment hardness, impact energy and microstructure in API X65 steel,” Int. J. Pressure Vessels Piping, 98, 8–15, 2012.
- A. Radovic, N. Bajic, and V. Grabulov, “Specific quality of the weld metal of welded joints of finegrained microalloyed steels,” Zavarivanje 96, 61–72, 1996.
- N. Bajic, V. Sijacki-Zeravcic, M. Rakin, and K. Kovacevic, “Structure optimization of weld metal and HAZ in microalloyed high strength steel welded joints,” Yucomat, Herceg Novi, 193–200, 2005.
- Bajic and, N.V. Šijaki-Žeravi, “The analysis of change of structural and mechanical properties of welded joints of microalloyed Nb/V steel grade by changing the composition of filler material,” Internat. Conf. On Welding, Belgrade, 2003.
- B.E. Rani Amitha, and J. Bharathibai Basu, “Green corrosion inhibitors - an overview,” Technical Report, National Aerospace Laboratories, Bangalore, India, 2009.
- M.A. Migahed, A.M. Al-Sabagh, E.A. Khamis, E.G. Zaki, “Quantum Chemical calculations, synthesis and corrosion inhibition efficiency of ethoxylated- [2- (2 - {2 - [2- (2 –benzen esulfonylaminoethylamino) - ethylamino] - ethylamino} - ethylamino) - ethyl] -4 - alkyl benzenesulfonamide on API X65 steel surface under H2S environment,” Journal of Molecular Liquids, 212, 360–371, 2015.
- http://w3.balikesir.edu.tr/~ay/lectures/km/lect ure1.pdf
- K.E. Hagedorn, R. Kaspar, and R. Kleine, “Untersuchungen zum einfluss des gefügesauf bruchmechanische kennwerte,” Steel Research, 61(10), 510-517, 1990.
- Z. Taş, “Termomekanik İşlem Görmüş Mikroalaşımlı Çeliklerin Kırılma Mekaniği - Kırılma Tokluğu- Açısından İncelenmesi, Doktora Tezi” YTÜ Fen Bilimleri Enstitüsü, İstanbul, 107, 2004.
- Tang J., Liu Z., Shi S, Chen X, “Evaluation of fracture toughness in different regions of weld joints using unloading compliance and normalization method”, Engineering Fracture Mechanics, 195: 1–12, 2018.
- Kingklang S., Uthaisangsuk V, “Plastic deformation and fracture behavior of X65 pipeline steel: Experiments and modeling”, Engineering Fracture Mechanics, 191:82- 101, 2018.
- Liu L., Xiao H., Li Q., Liu Y., Li P., Yang Z., Yu H, “Evaluation of the fracture toughness of X70 pipeline steel with ferritebainite microstructure”, Materials Science & Engineering A, 688:388–395, 2017.
- Maruschak P.O., Panin S.V.,. Chausov M.G., Bishchak R.T., Polyvana U.V, “Effect of long-term operation on steels of main gas pipeline. Reduction of static fracture toughness”, Journal of Natural Gas Science and Engineering, 38:182-186, 2017.
- Yonghe Y., Lei S. Zhen X. Hongsheng L., Xu C., Xin W., “Fracture toughness of the materials in welded joint of X80 pipeline steel”, Engineering Fracture Mechanics, 148:337–349, 2015.
- Yang Z., “The Fracture during Drop-Weight Tear Test of High Performance Pipeline Steel and Its Abnormal Fracture Appearance”, Procedia Materials Science, 3:1591–1598, 2014.
| APA | Asikuzun E, ÇETİNKAYA C, BOZ M, ADA H (2018). Fracture surface investigations of API pipes welded with parameters determined by Taguchi method. , 1392 - 1402. 10.16984/saufenbilder.397639 |
| Chicago | Asikuzun Elif,ÇETİNKAYA Cemil,BOZ MUSTAFA,ADA Hakan Fracture surface investigations of API pipes welded with parameters determined by Taguchi method. (2018): 1392 - 1402. 10.16984/saufenbilder.397639 |
| MLA | Asikuzun Elif,ÇETİNKAYA Cemil,BOZ MUSTAFA,ADA Hakan Fracture surface investigations of API pipes welded with parameters determined by Taguchi method. , 2018, ss.1392 - 1402. 10.16984/saufenbilder.397639 |
| AMA | Asikuzun E,ÇETİNKAYA C,BOZ M,ADA H Fracture surface investigations of API pipes welded with parameters determined by Taguchi method. . 2018; 1392 - 1402. 10.16984/saufenbilder.397639 |
| Vancouver | Asikuzun E,ÇETİNKAYA C,BOZ M,ADA H Fracture surface investigations of API pipes welded with parameters determined by Taguchi method. . 2018; 1392 - 1402. 10.16984/saufenbilder.397639 |
| IEEE | Asikuzun E,ÇETİNKAYA C,BOZ M,ADA H "Fracture surface investigations of API pipes welded with parameters determined by Taguchi method." , ss.1392 - 1402, 2018. 10.16984/saufenbilder.397639 |
| ISNAD | Asikuzun, Elif vd. "Fracture surface investigations of API pipes welded with parameters determined by Taguchi method". (2018), 1392-1402. https://doi.org/10.16984/saufenbilder.397639 |
| APA | Asikuzun E, ÇETİNKAYA C, BOZ M, ADA H (2018). Fracture surface investigations of API pipes welded with parameters determined by Taguchi method. Sakarya Üniversitesi Fen Bilimleri Enstitüsü Dergisi, 22(5), 1392 - 1402. 10.16984/saufenbilder.397639 |
| Chicago | Asikuzun Elif,ÇETİNKAYA Cemil,BOZ MUSTAFA,ADA Hakan Fracture surface investigations of API pipes welded with parameters determined by Taguchi method. Sakarya Üniversitesi Fen Bilimleri Enstitüsü Dergisi 22, no.5 (2018): 1392 - 1402. 10.16984/saufenbilder.397639 |
| MLA | Asikuzun Elif,ÇETİNKAYA Cemil,BOZ MUSTAFA,ADA Hakan Fracture surface investigations of API pipes welded with parameters determined by Taguchi method. Sakarya Üniversitesi Fen Bilimleri Enstitüsü Dergisi, vol.22, no.5, 2018, ss.1392 - 1402. 10.16984/saufenbilder.397639 |
| AMA | Asikuzun E,ÇETİNKAYA C,BOZ M,ADA H Fracture surface investigations of API pipes welded with parameters determined by Taguchi method. Sakarya Üniversitesi Fen Bilimleri Enstitüsü Dergisi. 2018; 22(5): 1392 - 1402. 10.16984/saufenbilder.397639 |
| Vancouver | Asikuzun E,ÇETİNKAYA C,BOZ M,ADA H Fracture surface investigations of API pipes welded with parameters determined by Taguchi method. Sakarya Üniversitesi Fen Bilimleri Enstitüsü Dergisi. 2018; 22(5): 1392 - 1402. 10.16984/saufenbilder.397639 |
| IEEE | Asikuzun E,ÇETİNKAYA C,BOZ M,ADA H "Fracture surface investigations of API pipes welded with parameters determined by Taguchi method." Sakarya Üniversitesi Fen Bilimleri Enstitüsü Dergisi, 22, ss.1392 - 1402, 2018. 10.16984/saufenbilder.397639 |
| ISNAD | Asikuzun, Elif vd. "Fracture surface investigations of API pipes welded with parameters determined by Taguchi method". Sakarya Üniversitesi Fen Bilimleri Enstitüsü Dergisi 22/5 (2018), 1392-1402. https://doi.org/10.16984/saufenbilder.397639 |