Effects of Chemical and Surface Modification on Mechanical and Chemical Properties of Polyester Fabrics
Yıl: 2018 Cilt: 6 Sayı: 4 Sayfa Aralığı: 1344 - 1353 Metin Dili: İngilizce İndeks Tarihi: 06-02-2020
Effects of Chemical and Surface Modification on Mechanical and Chemical Properties of Polyester Fabrics
Öz: Alkali treatment of polyester fabrics is a common chemical modification process for forming a fabric withdesirable qualities such as soft cloth, fabric regain, water absorbency, and fabric pilling with draping. However,if the optimization of the chemical treatment was not maintained, there could be serious decrease in mechanicalstrength of polyester fabrics. In this study, surface modification via low-temperature plasma application (<50 0C)was used as an alternative to chemical modification of polyester fabrics with alkaline treatment and the effects ofboth chemical and surface modification on mechanical and chemical properties of polyester fabrics wereinvestigated. Parameters of chemical modification such as exposure time and concentration of alkali were variedwhile different exposure time was used in plasma application as a surface modification treatment. Performancetests such as mechanical strength, loss of weight and hydrophilicity of polyester fabrics were tested after eachmodification. Scanning electron microscope (SEM) micrographs were characterized as well. According to thetest results; loss of weight of polyester fabrics after chemical modification was more than occurred right aftersurface modification. Advantages of surface modification on polyester fabrics were clearly seen in this study,especially when compared to high concentration alkali treatment. It was also considered that these functionalizedpolyester fabrics could be used as an alternative platform for 3DP (three-dimentional printing) applicationsbefore deposition of thepolymers.
Anahtar Kelime: Kimyasal ve Yüzey Modifikasyon İşlemlerinin Polyester Kumaşların Mekanik ve Kimyasal Özelliklerine Etkileri
Öz: Polyester kumaşların alkali ortamda işlem görmesi kumaşların yumuşak tutum, hidrofilik karakter kazanması, dökümlü bir kumaş haline gelmesi gibi istenen özelliklere sahip olmasını sağlayan alışılmış bir uygulamadır. Fakat yapılan bu kimyasal modifikasyon işleminin parametreleri optimize edilmediğinde, polyester kumaşların mekanik mukavemetlerinde ciddi düşüşler görülebilmektedir. Bu çalışmada, düşük sıcaklıkta yapılan (<50 0C) plazma aplikasyonu ile yüzey modifikasyon işlemi; polyester kumaşların kimyasal modifikasyon işlemlerine bir alternatif olarak kullanılmıştır ve her iki modifikasyon işleminin polyester kumaşların mekanik ve kimyasal özelliklerine olan etkileri incelenmiştir. Süre ve konsantrasyon gibi kimyasal modifikasyon işleminin parametreleri çeşitlendirilirken, yüzey modifikasyon işleminde kumaşlar farklı plazma işlem sürelerine tabi tutulmuştur. Her iki modifikasyondan sonra, polyester kumaşların mekanik özellikleri, hidrofilite değerleri ve ağırlık kayıpları gibi performans değerleri incelenmiş, taramalı elektron mikroskobu (SEM) görüntüleri alınmıştır. Test sonuçlarına göre; kimyasal modifikasyondan sonra kumaşlarda oluşan ağırlık kaybı plazma işlemi ile yapılan yüzey modifikasyonu işlemine oranla daha fazla olmuştur. Bu çalışmada, özellikle yüksek konsantrasyonda yapılan alkali işleme göre; polyester kumaşlara uygulanan yüzey modifikasyon işleminin pek çok avantajı görülmüştür. Fonksiyonelleştirilmiş bu polyester kumaşların üç boyutlu baskı uygulamalarında polimer aktarılmadan önce alternatif bir platform olarak kullanılabileceği düşünülmüştü
Anahtar Kelime: Belge Türü: Makale Makale Türü: Araştırma Makalesi Erişim Türü: Erişime Açık
- D. Jayshree, R. Kumar, and H. C. Srivastava, “Studies on Modification of Polyester Fabrics I: Alkaline Hydrolysis,” Journal of Applied Polymer Science, vol.33, no. 2, pp. 455-477, 1987.
- K. M. Haghighat and M. Nouri, “Effects of sodium hydroxide and calcium hydroxide on polyester fabrics,” Journal of Applied Polymer Science, vol. 72, no. 5, pp. 631-637,1999.
- S. R. Shukla and M. R. Mathur, “Action of Alkali on Polybutylene Terephthalate and Polyethylene Terephthalate Polyesters,” Journal of Applied Polymer Science, vol. 75, no. 9, pp. 1097- 1102, 2000.
- S. Natarajan and J. Jeyakodi Moses, “Surface modification of polyester fabric using polyvinyl alcohol in alkaline medium,” Indian Journal of Fibre& Textile Research, vol.37, no. 4, pp. 287-291, 2012.
- M. Kodrić, D. Đorđević, S. Konstantinović, and M. Kostić, “The modification of the polyester knitted fabric for more economic dyeing,” Advanced Technologies, vol. 6 no. 2, pp. 60-66, 2017.
- C. Kahraman, “Polyester alkalizasyonu yalnızca moda eğilimi değil”, Tekstil ve Makine, vol. 2 no.8, pp. 102-105, 1988.
- S. Perincek, A. E. Uzgur, K. Duran, A. Dogan, A. E. Korlu and İ. M. Bahtiyari, “Design Parameter Investigation of Industrial Size Ultrasound Textile Treatment Bath,” Ultrasonics sonochemistry, vol.16, no. 1,pp. 184-189, 2009.
- P. Bajaj, “Finishing of Textile Materials,” Journal of Applied Polymer Science, vol. 83, no.3, pp. 631-659, 2002. 1353
- T. H. C. Costa, M. C. Feitor, Jr, C. Alves, P. B. Freire, and C. M. De Bezerra, "Effects of Gas Composition During Plasma Modification of Polyester Fabrics." Journal of Materials Processing Technology ,vol. 173, no. 1, pp. 40-43, 2006.
- R. Rajendra, N. Deshmukh and V. Bhat, “The Mechanism of Adhesion and Printability of Plasma Processed PET Films,” Materials Research Innovations, vol. 7, no. 5, pp. 283–290, 2003.
- K. Qi, JH .Xin and WA. Daoud, “Functionalizing Polyester Fiber with A Self-Cleaning Property Using Anatase TiO2 and Low-Temperature Plasma Treatment” International Journal of Applied Ceramic Technology, vol. 4, no. 6, pp. 554–563, 2007.
- A. Vesel, I. Junkar, U. Cvelbar, J. Kovac, and M. Mozetic, "Surface Modification of Polyester by Oxygen and Nitrogen‐Plasma Treatment," Surface and interface analysis, vol. 40, no. 11, pp. 1444- 1453, 2008.
- B. Çotur, and Sezer. H. K., "Current 3 Dimensional Printing Technologies Used in Scaffold Design in Tissue Engineering, "Duzce University Journal of Science & Technology, vol. 5, no. 2, pp. 548-564, 2017.
- K. Çelik, and A. Özkan, "Eklemeli İmalat Yöntemleri İle Üretim ve Onarım Uygulamaları," Duzce University Journal of Science & Technology,vol.5, no. 1, pp. 107-121, 2017.
- H. A. Çetindağ, Toktaş İ. and M. T. ÖZKAN. "3 Boyutlu Baskısı Yapılacak Ankastre Kirişlerin Eşit Miktarda Filament Kullanımı ile Eğilme Mukavemetine Göre Kesit Geometrisi Optimizasyonu," Duzce University Journal of Science & Technology, vol. 5, no. 2, pp. 466-476, 2017.
- R. H. Sanatgar, C. Campagne and V. Nierstrasz. “Investigation of the Adhesion Properties of Direct 3d Printing of Polymers and Nanocomposites on Textiles: Effect of FDM Printing Process Parameters,”Applied Surface Science, vol. 403, no. 2, pp. 551-563, 2017.
| APA | BAŞYİĞİT Z (2018). Effects of Chemical and Surface Modification on Mechanical and Chemical Properties of Polyester Fabrics. , 1344 - 1353. |
| Chicago | BAŞYİĞİT Zeynep ÖMEROĞULLARI Effects of Chemical and Surface Modification on Mechanical and Chemical Properties of Polyester Fabrics. (2018): 1344 - 1353. |
| MLA | BAŞYİĞİT Zeynep ÖMEROĞULLARI Effects of Chemical and Surface Modification on Mechanical and Chemical Properties of Polyester Fabrics. , 2018, ss.1344 - 1353. |
| AMA | BAŞYİĞİT Z Effects of Chemical and Surface Modification on Mechanical and Chemical Properties of Polyester Fabrics. . 2018; 1344 - 1353. |
| Vancouver | BAŞYİĞİT Z Effects of Chemical and Surface Modification on Mechanical and Chemical Properties of Polyester Fabrics. . 2018; 1344 - 1353. |
| IEEE | BAŞYİĞİT Z "Effects of Chemical and Surface Modification on Mechanical and Chemical Properties of Polyester Fabrics." , ss.1344 - 1353, 2018. |
| ISNAD | BAŞYİĞİT, Zeynep ÖMEROĞULLARI. "Effects of Chemical and Surface Modification on Mechanical and Chemical Properties of Polyester Fabrics". (2018), 1344-1353. |
| APA | BAŞYİĞİT Z (2018). Effects of Chemical and Surface Modification on Mechanical and Chemical Properties of Polyester Fabrics. Düzce Üniversitesi Bilim ve Teknoloji Dergisi, 6(4), 1344 - 1353. |
| Chicago | BAŞYİĞİT Zeynep ÖMEROĞULLARI Effects of Chemical and Surface Modification on Mechanical and Chemical Properties of Polyester Fabrics. Düzce Üniversitesi Bilim ve Teknoloji Dergisi 6, no.4 (2018): 1344 - 1353. |
| MLA | BAŞYİĞİT Zeynep ÖMEROĞULLARI Effects of Chemical and Surface Modification on Mechanical and Chemical Properties of Polyester Fabrics. Düzce Üniversitesi Bilim ve Teknoloji Dergisi, vol.6, no.4, 2018, ss.1344 - 1353. |
| AMA | BAŞYİĞİT Z Effects of Chemical and Surface Modification on Mechanical and Chemical Properties of Polyester Fabrics. Düzce Üniversitesi Bilim ve Teknoloji Dergisi. 2018; 6(4): 1344 - 1353. |
| Vancouver | BAŞYİĞİT Z Effects of Chemical and Surface Modification on Mechanical and Chemical Properties of Polyester Fabrics. Düzce Üniversitesi Bilim ve Teknoloji Dergisi. 2018; 6(4): 1344 - 1353. |
| IEEE | BAŞYİĞİT Z "Effects of Chemical and Surface Modification on Mechanical and Chemical Properties of Polyester Fabrics." Düzce Üniversitesi Bilim ve Teknoloji Dergisi, 6, ss.1344 - 1353, 2018. |
| ISNAD | BAŞYİĞİT, Zeynep ÖMEROĞULLARI. "Effects of Chemical and Surface Modification on Mechanical and Chemical Properties of Polyester Fabrics". Düzce Üniversitesi Bilim ve Teknoloji Dergisi 6/4 (2018), 1344-1353. |