Production and characterization of ternary sheep hydroxyapatite (SHA)-wollastonite (W)-commercial inert glass (CIG) biocomposite
Yıl: 2019 Cilt: 5 Sayı: 2 Sayfa Aralığı: 167 - 174 Metin Dili: İngilizce DOI: 10.17515/resm2018.68is0919 İndeks Tarihi: 01-07-2020
Production and characterization of ternary sheep hydroxyapatite (SHA)-wollastonite (W)-commercial inert glass (CIG) biocomposite
Öz: Hydroxyapatite [HA] is the most widely accepted biomaterial for the repair andreconstruction of bone tissue defects. It has all the characteristic features ofbiomaterials such as biocompatible, bioactive, osteoconductive, nontoxic, noninflammatory and non-immunogenic properties. It has low mechanicalproperties for load bearing applications. HA must be reinforced with otherceramics or metals to produce more load resistible composites. HA also can beproduced from natural materials such as bovine, sheep, chicken, human bones,fish bones with simple calcination method. In this study, 5 wt% wollastonite and5 wt% commercial inert glass were added to sheep hydroxyapatite together toimprove mechanical properties. Mechanical properties of composite increasedwith increasing sintering temperature. The highest Vickers microhardness andcompression strength values were obtained with SHA-5 wt% wollastonite- 5 wt% CIG composite sintered at 1300ºC as 197 HV and 94 MPa, respectively.
Anahtar Kelime: Belge Türü: Makale Makale Türü: Araştırma Makalesi Erişim Türü: Erişime Açık
- [1] Stipniece L. Salma-Ancane K. Putnins A. and Berzina-Cimdina L. Evaluation of Sr-and/or Mg-containing Hydroxyapatite Behavior in Simulated Body Fluid, Key Engineering Materials, 2015; 631: 61 – 66. https://doi.org/10.4028/www.scientific.net/KEM.631.61
- [2] Skwarek E. Bolbukh Y. Janusz W. and Tertykh V. Hydroxyapatite Composites with Multiwalled Carbon Nanotubes. Adsorption Science & Technology, 2017; 35(5-6): 534 – 544. https://doi.org/10.1177/0263617417700637
- [3] Encinas-Romero MA. Aguayo-Salinas S. Valenzuela-Garcia JL. Payan SR. and CastillonBarraza FF. Mechanical and Bioactive Behavior of Hydroxyapatite-Wollastonite Sintered Composites. Int, J. Appl. Ceram. Technol., 2010; 7(2): 164-177. https://doi.org/10.1111/j.1744-7402.2009.02377.x
- [4] Demirkol N. Physical and Mechanical Properties of Hydroxyapatite-WollastoniteTitania Composites. Journal of Turkish Ceramic Federation, 2016; 49: 102-109.
- [5] Lin K. Zhang M. Zhai W. Qu H. Chang J. Fabrication and Characterization of Hydroxyapatite/Wollastonite Composite Bioceramics with Controllable Properties for Hard Tissue Repair. Journal of the American Ceramic Society, 2011; 94(1): 99-105. https://doi.org/10.1111/j.1551-2916.2010.04046.x
- [6] Harabi A. Chehlatt S. Preperation Process of a Highly Resistant Wollastonite Bioceramics Using Local Raw Materials. Journal of Thermal Analysis and Calorimetry, 2013; 111(1): 203-211. https://doi.org/10.1007/s10973-012-2242-5
- [7] Demirkol N. Oktar F.N. Kayali E.S. Influence of Commercial Inert Glass Addition on the Mechanical Properties of Commercial Synthetic Hydroxyapatite. Acta Physica Polonica A, 2013; 123(2): 427-429. https://doi.org/10.12693/APhysPolA.123.427
- [8] Rocha D.N. Oliveira Cruz L.R. Prado Neto J.L. Elmassalami Ayad N.M. Gobbo L.A. and Silva M.H.P. Production and Characterization of Hydroxyapatite/Niobo Phosphate Glass Scaffold. Key Engineering Materials, 2014; 587: 128-131. https://doi.org/10.4028/www.scientific.net/KEM.587.128
- [9] Salman S. Oktar F.N. Gunduz O. Agathopoulos S. Ovecoglu M.L. Kayali E.S. Sintering Effect on Mechanical Properties of Composites Made of Bovine Hydroxyapatite(BHA) and Commercial Inert Glass (CIG). Key Engineering Materials, 2007; 330-332: 189-192. https://doi.org/10.4028/www.scientific.net/KEM.330-332.189
- [10] British Standard Non-metallic materials for surgical implants. Part 2. Specification for [1] Stipniece L. Salma-Ancane K. Putnins A. and Berzina-Cimdina L. Evaluation of Sr-and/or Mg-containing Hydroxyapatite Behavior in Simulated Body Fluid, Key Engineering Materials, 2015; 631: 61 – 66. https://doi.org/10.4028/www.scientific.net/KEM.631.61 [2] Skwarek E. Bolbukh Y. Janusz W. and Tertykh V. Hydroxyapatite Composites with Multiwalled Carbon Nanotubes. Adsorption Science & Technology, 2017; 35(5-6): 534 – 544. https://doi.org/10.1177/0263617417700637 [3] Encinas-Romero MA. Aguayo-Salinas S. Valenzuela-Garcia JL. Payan SR. and CastillonBarraza FF. Mechanical and Bioactive Behavior of Hydroxyapatite-Wollastonite Sintered Composites. Int, J. Appl. Ceram. Technol., 2010; 7(2): 164-177. https://doi.org/10.1111/j.1744-7402.2009.02377.x [4] Demirkol N. Physical and Mechanical Properties of Hydroxyapatite-WollastoniteTitania Composites. Journal of Turkish Ceramic Federation, 2016; 49: 102-109. [5] Lin K. Zhang M. Zhai W. Qu H. Chang J. Fabrication and Characterization of Hydroxyapatite/Wollastonite Composite Bioceramics with Controllable Properties for Hard Tissue Repair. Journal of the American Ceramic Society, 2011; 94(1): 99-105. https://doi.org/10.1111/j.1551-2916.2010.04046.x [6] Harabi A. Chehlatt S. Preperation Process of a Highly Resistant Wollastonite Bioceramics Using Local Raw Materials. Journal of Thermal Analysis and Calorimetry, 2013; 111(1): 203-211. https://doi.org/10.1007/s10973-012-2242-5 [7] Demirkol N. Oktar F.N. Kayali E.S. Influence of Commercial Inert Glass Addition on the Mechanical Properties of Commercial Synthetic Hydroxyapatite. Acta Physica Polonica A, 2013; 123(2): 427-429. https://doi.org/10.12693/APhysPolA.123.427 [8] Rocha D.N. Oliveira Cruz L.R. Prado Neto J.L. Elmassalami Ayad N.M. Gobbo L.A. and Silva M.H.P. Production and Characterization of Hydroxyapatite/Niobo Phosphate Glass Scaffold. Key Engineering Materials, 2014; 587: 128-131. https://doi.org/10.4028/www.scientific.net/KEM.587.128 [9] Salman S. Oktar F.N. Gunduz O. Agathopoulos S. Ovecoglu M.L. Kayali E.S. Sintering Effect on Mechanical Properties of Composites Made of Bovine Hydroxyapatite(BHA) and Commercial Inert Glass (CIG). Key Engineering Materials, 2007; 330-332: 189-192. https://doi.org/10.4028/www.scientific.net/KEM.330-332.189 [10] British Standard Non-metallic materials for surgical implants. Part 2. Specification for [11] Demirkol N. Production and Characterization of Sheep Hydroxyapatite Composites, Yalın Publication, 2016; 59-62. [12] Bulut B. Erkmen Z.E. Kayali E.S. Biocompatibility of Hydroxyapatite-Alumina and Hydroxyapatite-Zirconia Composites Including Commercial Inert Glass (CIG) as a Ternary Component. J. Ceram. Sci. Tech. 2016; 07[03]: 263-276. [13] Oktar FN. Goller G. Sintering Effects on Mechanical Properties of Glass-Reinforced Hydroxyapatite Composites. Ceramics International. 2002; 28: 617-621. https://doi.org/10.1016/S0272-8842(02)00017-2 [14] Sidane D. Rammal H. Beljabbar a. Gangloff S.C. Chicot D. Velard F. Khireddine H. Montagne A. Kerdjoudj H. Biocompatibility of Sol-Gel Hydroxyapatite-Titania Composite and Bilayer Coatings. Materials Science and Engineering: C, 2017; 72: 650- 658. https://doi.org/10.1016/j.msec.2016.11.129 [11] Demirkol N. Production and Characterization of Sheep Hydroxyapatite Composites, Yalın Publication, 2016; 59-62.
- [12] Bulut B. Erkmen Z.E. Kayali E.S. Biocompatibility of Hydroxyapatite-Alumina and Hydroxyapatite-Zirconia Composites Including Commercial Inert Glass (CIG) as a Ternary Component. J. Ceram. Sci. Tech. 2016; 07[03]: 263-276.
- [13] Oktar FN. Goller G. Sintering Effects on Mechanical Properties of Glass-Reinforced Hydroxyapatite Composites. Ceramics International. 2002; 28: 617-621. https://doi.org/10.1016/S0272-8842(02)00017-2
- [14] Sidane D. Rammal H. Beljabbar a. Gangloff S.C. Chicot D. Velard F. Khireddine H. Montagne A. Kerdjoudj H. Biocompatibility of Sol-Gel Hydroxyapatite-Titania Composite and Bilayer Coatings. Materials Science and Engineering: C, 2017; 72: 650- 658. https://doi.org/10.1016/j.msec.2016.11.129.
| APA | Demirkol N, TURAN M (2019). Production and characterization of ternary sheep hydroxyapatite (SHA)-wollastonite (W)-commercial inert glass (CIG) biocomposite. , 167 - 174. 10.17515/resm2018.68is0919 |
| Chicago | Demirkol Nermin,TURAN MERVE Production and characterization of ternary sheep hydroxyapatite (SHA)-wollastonite (W)-commercial inert glass (CIG) biocomposite. (2019): 167 - 174. 10.17515/resm2018.68is0919 |
| MLA | Demirkol Nermin,TURAN MERVE Production and characterization of ternary sheep hydroxyapatite (SHA)-wollastonite (W)-commercial inert glass (CIG) biocomposite. , 2019, ss.167 - 174. 10.17515/resm2018.68is0919 |
| AMA | Demirkol N,TURAN M Production and characterization of ternary sheep hydroxyapatite (SHA)-wollastonite (W)-commercial inert glass (CIG) biocomposite. . 2019; 167 - 174. 10.17515/resm2018.68is0919 |
| Vancouver | Demirkol N,TURAN M Production and characterization of ternary sheep hydroxyapatite (SHA)-wollastonite (W)-commercial inert glass (CIG) biocomposite. . 2019; 167 - 174. 10.17515/resm2018.68is0919 |
| IEEE | Demirkol N,TURAN M "Production and characterization of ternary sheep hydroxyapatite (SHA)-wollastonite (W)-commercial inert glass (CIG) biocomposite." , ss.167 - 174, 2019. 10.17515/resm2018.68is0919 |
| ISNAD | Demirkol, Nermin - TURAN, MERVE. "Production and characterization of ternary sheep hydroxyapatite (SHA)-wollastonite (W)-commercial inert glass (CIG) biocomposite". (2019), 167-174. https://doi.org/10.17515/resm2018.68is0919 |
| APA | Demirkol N, TURAN M (2019). Production and characterization of ternary sheep hydroxyapatite (SHA)-wollastonite (W)-commercial inert glass (CIG) biocomposite. Research on Engineering Structures and Materials, 5(2), 167 - 174. 10.17515/resm2018.68is0919 |
| Chicago | Demirkol Nermin,TURAN MERVE Production and characterization of ternary sheep hydroxyapatite (SHA)-wollastonite (W)-commercial inert glass (CIG) biocomposite. Research on Engineering Structures and Materials 5, no.2 (2019): 167 - 174. 10.17515/resm2018.68is0919 |
| MLA | Demirkol Nermin,TURAN MERVE Production and characterization of ternary sheep hydroxyapatite (SHA)-wollastonite (W)-commercial inert glass (CIG) biocomposite. Research on Engineering Structures and Materials, vol.5, no.2, 2019, ss.167 - 174. 10.17515/resm2018.68is0919 |
| AMA | Demirkol N,TURAN M Production and characterization of ternary sheep hydroxyapatite (SHA)-wollastonite (W)-commercial inert glass (CIG) biocomposite. Research on Engineering Structures and Materials. 2019; 5(2): 167 - 174. 10.17515/resm2018.68is0919 |
| Vancouver | Demirkol N,TURAN M Production and characterization of ternary sheep hydroxyapatite (SHA)-wollastonite (W)-commercial inert glass (CIG) biocomposite. Research on Engineering Structures and Materials. 2019; 5(2): 167 - 174. 10.17515/resm2018.68is0919 |
| IEEE | Demirkol N,TURAN M "Production and characterization of ternary sheep hydroxyapatite (SHA)-wollastonite (W)-commercial inert glass (CIG) biocomposite." Research on Engineering Structures and Materials, 5, ss.167 - 174, 2019. 10.17515/resm2018.68is0919 |
| ISNAD | Demirkol, Nermin - TURAN, MERVE. "Production and characterization of ternary sheep hydroxyapatite (SHA)-wollastonite (W)-commercial inert glass (CIG) biocomposite". Research on Engineering Structures and Materials 5/2 (2019), 167-174. https://doi.org/10.17515/resm2018.68is0919 |