Preparation of thin $Bi_2Sr_2CaCu_2O_x$ (2212) film and electrical measurements
Yıl: 1996 Cilt: 20 Sayı: 9 Sayfa Aralığı: 1012 - 1016 Metin Dili: İngilizce İndeks Tarihi: 29-07-2022
Preparation of thin $Bi_2Sr_2CaCu_2O_x$ (2212) film and electrical measurements
Öz: A thin film with the nominal composition of .$Bi_2Sr_2CaCu_2O_x$ (2212) was prepared on a MgO single crystal substrate by electron beam evaporation technique. The film, analyzed by x-ray diffraction, showed a preferential orientation with the c-axis prependicular to the substrate. The existence of at least two phases was seen from x-ray analysis. Electrical measurement was performed on the thin film of 2212 composition. The resistivity was confirmed to be smaller then $0.20x10^{-4}Omega$.cm by using the van der Pauw method at 300K and critical current density was in excess of $1.2xl0^4 A/cm2$ at 38K in zero field.
Anahtar Kelime: Konular:
Belge Türü: Makale Makale Türü: Araştırma Makalesi Erişim Türü: Erişime Açık
0
0
0
| APA | VARILCI A, YANMAZ E, MUTLU I (1996). Preparation of thin $Bi_2Sr_2CaCu_2O_x$ (2212) film and electrical measurements. , 1012 - 1016. |
| Chicago | VARILCI A.,YANMAZ E.,MUTLU I. H. Preparation of thin $Bi_2Sr_2CaCu_2O_x$ (2212) film and electrical measurements. (1996): 1012 - 1016. |
| MLA | VARILCI A.,YANMAZ E.,MUTLU I. H. Preparation of thin $Bi_2Sr_2CaCu_2O_x$ (2212) film and electrical measurements. , 1996, ss.1012 - 1016. |
| AMA | VARILCI A,YANMAZ E,MUTLU I Preparation of thin $Bi_2Sr_2CaCu_2O_x$ (2212) film and electrical measurements. . 1996; 1012 - 1016. |
| Vancouver | VARILCI A,YANMAZ E,MUTLU I Preparation of thin $Bi_2Sr_2CaCu_2O_x$ (2212) film and electrical measurements. . 1996; 1012 - 1016. |
| IEEE | VARILCI A,YANMAZ E,MUTLU I "Preparation of thin $Bi_2Sr_2CaCu_2O_x$ (2212) film and electrical measurements." , ss.1012 - 1016, 1996. |
| ISNAD | VARILCI, A. vd. "Preparation of thin $Bi_2Sr_2CaCu_2O_x$ (2212) film and electrical measurements". (1996), 1012-1016. |
| APA | VARILCI A, YANMAZ E, MUTLU I (1996). Preparation of thin $Bi_2Sr_2CaCu_2O_x$ (2212) film and electrical measurements. Turkish Journal of Physics, 20(9), 1012 - 1016. |
| Chicago | VARILCI A.,YANMAZ E.,MUTLU I. H. Preparation of thin $Bi_2Sr_2CaCu_2O_x$ (2212) film and electrical measurements. Turkish Journal of Physics 20, no.9 (1996): 1012 - 1016. |
| MLA | VARILCI A.,YANMAZ E.,MUTLU I. H. Preparation of thin $Bi_2Sr_2CaCu_2O_x$ (2212) film and electrical measurements. Turkish Journal of Physics, vol.20, no.9, 1996, ss.1012 - 1016. |
| AMA | VARILCI A,YANMAZ E,MUTLU I Preparation of thin $Bi_2Sr_2CaCu_2O_x$ (2212) film and electrical measurements. Turkish Journal of Physics. 1996; 20(9): 1012 - 1016. |
| Vancouver | VARILCI A,YANMAZ E,MUTLU I Preparation of thin $Bi_2Sr_2CaCu_2O_x$ (2212) film and electrical measurements. Turkish Journal of Physics. 1996; 20(9): 1012 - 1016. |
| IEEE | VARILCI A,YANMAZ E,MUTLU I "Preparation of thin $Bi_2Sr_2CaCu_2O_x$ (2212) film and electrical measurements." Turkish Journal of Physics, 20, ss.1012 - 1016, 1996. |
| ISNAD | VARILCI, A. vd. "Preparation of thin $Bi_2Sr_2CaCu_2O_x$ (2212) film and electrical measurements". Turkish Journal of Physics 20/9 (1996), 1012-1016. |