Evaluation Of BIS-GMA Release In Different Types Of Composites
Yıl: 2021 Cilt: 14 Sayı: 1 Sayfa Aralığı: 299 - 305 Metin Dili: İngilizce DOI: 10.18185/erzifbed.865816 İndeks Tarihi: 02-03-2022
Evaluation Of BIS-GMA Release In Different Types Of Composites
Öz: BIS-GMA is frequently is involved in the structure of composite materials and may remain unpolymerized after polymerization. Residual Bis-GMA has harmful effects, it is crucial to determine the amounts released monomer from dental materials. The aim of this study is to compare residual BIS-GMA amounts in three types of composite. A total of 45 (n=15) composite (Filtek Ultimate Universal Restorative,3M ESPE,Germany), flowable composite (Nextcomp Flow,Meta Biomed,Kore), bulk fill composite(Tetric N Ceram, Ivoclar,Lichtenstein) cylindrical samples were polymerized in Teflon molds in accordance with the manufacturer's instructions. The samples were placed in 1.5ml ethanol (Carlo Erba, Pharm. Grade, 99.9%) and kept at 37oC. Monomer release of the samples was evaluated on the first, third and seventh days using the High Performance Liquid Chromatography technique. BIS-GMA release was shown with the highest amounts within all groups on the first day. The elution in composite fillings was significantly lower than the other materials on the first day(p<0.05). The highest total emission rates were observed in the flowable composite. The material selected in clinical practice should be considered because the monomer release may vary depending on the composite type.
Anahtar Kelime: Farklı Kompozit Dolguların BIS-GMA Salınımlarının İncelenmesi
Öz: Kompozit malzemelerin sıklıkla yapısında yer alan BIS-GMA, polimerizasyondan sonar reaksiyona girmeden kalabilmektedir. Artık monomerlerin bilinen zararlı etkileri nedeniyle, dental malzemelerden salınan monomer miktarlarının belirlenmesi çok önemlidir. Mevcut çalışmanın amacı, kompozitrezin, akışkan kompozitve bulk fill kompozit materyallerden salınan BIS-GMA miktarlarının değerlendirilmesidir. Toplamda 45 adet kompozit (Filtek Ultimate Universal Restorative,3M ESPE,Germany), akışkan kompozit (NextcompFlow,MetaBiomed,Kore), bulk fill kompozit (Tetric N Ceram, Ivoclar,Lichtenstein) silindirik örnek (n=15)Teflon kalıplarda üretici firma talimatları doğrultusunda polymerize edildi. Örnekler 1,5ml etanol (Carlo Erba, Pharm. Grade, 99.9%) içine yerleştirilerek 37oC’de muhafaza edildi. Örneklerin monomer salınımıYüksekPerformanslıSıvıKromatografitekniğikullanılarakbirinci, üçüncü ve yedinci günde değerlendirildi. BIS-GMA salınımının ilk gün tüm gruplarda en yüksek miktarlarda görülmüştür. Kompozit grubunda elüsyon birinci gün diğer malzemelere göre anlamlı olarak düşük bulunmuştur(p<0.05). En yüksek toplam salınım oranları akışkan kompozitte görülmüştür. Klinikte malzeme seçiminde, monomer salınımının kompozit tipine göre değişebileceği dikkate alınmalıdır.
Anahtar Kelime: Belge Türü: Makale Makale Türü: Araştırma Makalesi Erişim Türü: Erişime Açık
- Schwengberg S, Bohlen H, Kleinsasser N. 2005. In vitro embryotoxicity assessment with dental restorative materials. J Dent. 33(1):49-55.
- Van Landuyt KLL, Nawrot T, Geebelen B, et al. 2011. How much do resin-based dental materials release? A meta-analytical approach. Dent Mater. 27(8):723-47.
- Goldberg M. 2008. In vitro and in vivo studies on the toxicity of dental resin components: a review. Clin Oral Investig. 12(1):1-8.
- Schweikl H, Hartmann A, Hiller KA, et al. 2007. Inhibition of TEGDMA and HEMAinduced genotoxicity and cell cycle arrest by N-acetylcysteine. Dent Mater. 23(6):688-695.
- Al-Hiyasat AS, Darmani H. 2006. In vivo effects of BISGMA—a component of dental composite—on male mouse reproduction and fertility. J Biomed Mater Res Part A. 78A(1):66-72.
- Söderholm KJ, Mariotti A. 1999. BISGMA-based resins in dentistry: Are they safe? J Am Dent Assoc. 130(2):201-209.
- Marzouk T, Sathyanarayana S, Kim AS, Seminario AL, McKinney CM. 2019. A Systematic Review of Exposure to Bisphenol A from Dental Treatment. JDR Clin Transl Res. 4(2):106-115.
- Akyüz S, Yarat A, Egil E, 2011. Marmara Üniversitesi Diş Hekimliği Fakültesi M, Temel Tıp Bilimleri Bölümü ve. BisfenolA İçerikli Dental Materyallere Güncel Yaklaşım. Marmara Üniversitesi Sağlık Bilim Enst Derg. 1(3):190-195.
- Putzeys E, Nys S De, Cokic SM, et al. 2019. Long-term elution of monomers from resin-based dental composites. Dent Mater. 35(3):477-485.
- Alshali RZ, Salim NA, Sung R, Satterthwaite JD, Silikas N. 2015. Analysis of long-term monomer elution from bulkfill and conventional resin-composites using high performance liquid chromatography. Dent Mater. 31(12):1587-98.
- Moilanen LH, Dahms JK, Hoberman AM. 2013. Reproductive toxicity evaluation of the dental resin monomer bisphenol a glycidyl methacrylate (CAS 1565-94-2) in Mice. Int J Toxicol. 32(6):415-425.
- Polydorou O, König A, Hellwig E, Kümmerer K. 2009. Long-term release of monomers from modern dental-composite materials. Eur J Oral Sci. 117(1):68-75.
- Ferracane JL. 1994. Elution of leachable components from composites. J Oral Rehabil. 21(4):441-452.
- Reichl FX, Seiss M, Kleinsasser N, et al. 2008. Distribution and excretion of BisGMA in guinea pigs. J Dent Res. 87(4):378-380.
- Moharamzadeh K, Van Noort R, Brook IM, Scutt AM. 2007. HPLC analysis of components released from dental composites with different resin compositions using different extraction media. In: Journal of Materials Science: Materials in Medicine. Vol 18. J Mater Sci Mater Med;:133-137.
| APA | Karaca S, OZDOKUR K, EGIL E, CEYRAN E, Duman C (2021). Evaluation Of BIS-GMA Release In Different Types Of Composites. , 299 - 305. 10.18185/erzifbed.865816 |
| Chicago | Karaca Serhat,OZDOKUR KEMAL VOLKAN,EGIL EDIBE,CEYRAN Ertuğrul,Duman Canan Evaluation Of BIS-GMA Release In Different Types Of Composites. (2021): 299 - 305. 10.18185/erzifbed.865816 |
| MLA | Karaca Serhat,OZDOKUR KEMAL VOLKAN,EGIL EDIBE,CEYRAN Ertuğrul,Duman Canan Evaluation Of BIS-GMA Release In Different Types Of Composites. , 2021, ss.299 - 305. 10.18185/erzifbed.865816 |
| AMA | Karaca S,OZDOKUR K,EGIL E,CEYRAN E,Duman C Evaluation Of BIS-GMA Release In Different Types Of Composites. . 2021; 299 - 305. 10.18185/erzifbed.865816 |
| Vancouver | Karaca S,OZDOKUR K,EGIL E,CEYRAN E,Duman C Evaluation Of BIS-GMA Release In Different Types Of Composites. . 2021; 299 - 305. 10.18185/erzifbed.865816 |
| IEEE | Karaca S,OZDOKUR K,EGIL E,CEYRAN E,Duman C "Evaluation Of BIS-GMA Release In Different Types Of Composites." , ss.299 - 305, 2021. 10.18185/erzifbed.865816 |
| ISNAD | Karaca, Serhat vd. "Evaluation Of BIS-GMA Release In Different Types Of Composites". (2021), 299-305. https://doi.org/10.18185/erzifbed.865816 |
| APA | Karaca S, OZDOKUR K, EGIL E, CEYRAN E, Duman C (2021). Evaluation Of BIS-GMA Release In Different Types Of Composites. Erzincan Üniversitesi Fen Bilimleri Enstitüsü Dergisi, 14(1), 299 - 305. 10.18185/erzifbed.865816 |
| Chicago | Karaca Serhat,OZDOKUR KEMAL VOLKAN,EGIL EDIBE,CEYRAN Ertuğrul,Duman Canan Evaluation Of BIS-GMA Release In Different Types Of Composites. Erzincan Üniversitesi Fen Bilimleri Enstitüsü Dergisi 14, no.1 (2021): 299 - 305. 10.18185/erzifbed.865816 |
| MLA | Karaca Serhat,OZDOKUR KEMAL VOLKAN,EGIL EDIBE,CEYRAN Ertuğrul,Duman Canan Evaluation Of BIS-GMA Release In Different Types Of Composites. Erzincan Üniversitesi Fen Bilimleri Enstitüsü Dergisi, vol.14, no.1, 2021, ss.299 - 305. 10.18185/erzifbed.865816 |
| AMA | Karaca S,OZDOKUR K,EGIL E,CEYRAN E,Duman C Evaluation Of BIS-GMA Release In Different Types Of Composites. Erzincan Üniversitesi Fen Bilimleri Enstitüsü Dergisi. 2021; 14(1): 299 - 305. 10.18185/erzifbed.865816 |
| Vancouver | Karaca S,OZDOKUR K,EGIL E,CEYRAN E,Duman C Evaluation Of BIS-GMA Release In Different Types Of Composites. Erzincan Üniversitesi Fen Bilimleri Enstitüsü Dergisi. 2021; 14(1): 299 - 305. 10.18185/erzifbed.865816 |
| IEEE | Karaca S,OZDOKUR K,EGIL E,CEYRAN E,Duman C "Evaluation Of BIS-GMA Release In Different Types Of Composites." Erzincan Üniversitesi Fen Bilimleri Enstitüsü Dergisi, 14, ss.299 - 305, 2021. 10.18185/erzifbed.865816 |
| ISNAD | Karaca, Serhat vd. "Evaluation Of BIS-GMA Release In Different Types Of Composites". Erzincan Üniversitesi Fen Bilimleri Enstitüsü Dergisi 14/1 (2021), 299-305. https://doi.org/10.18185/erzifbed.865816 |