Urfa stone has been used as an important building material in Şanlıurfa since ancient times due to its aesthetic appearance, easy processing, thermal insulation and durability properties. With the widespread use of concrete today, Urfa stone has lost its importance. In this research, it was investigated whether Urfa stone obtained from Şanlıurfa quarries, processed by hand and CNC machine, can be used as a design element in urban furniture. For this purpose , related to mineralogical and petrographic properties and chemical, physico-mechanical and petrophysical properties, a range of testing and analysis of engineering properties were carried out on building block samples. Urfa stone is in crystalline form and has a sparite texture containing 55.31% CaO and 0.24% SiO2. Porosity ratio is 16.50%, specific gravity is 2450 kg / m3, water absorption amount is 9.15%, compressive strength is 19.70 MPa, bending strength is 5.21 MPa and impact strength is 4.05 kPa. In petrophysical properties, Δ (percentage change in properties) values after freze-thaw test were found between 1.63% and 16.14%, and Δ values after salt crystallization test were found between 3.27% and 24.57%. According to this property change (%), it is more resistant to deterioration than other natural stones originating from calcium carbonate. The usage performance of Urfa stone in urban furniture has been proven to be good according to the tests of engineering properties. As a result of the study, it was determined that the designed urban furniture can be produced with Urfa stone which can be easily processed by hand or CNC machine.